INCOLOY alloys belong to the category of super austenitic stainless steels. These alloys have nickel-chromium-iron as the base metals, with additives such as molybdenum, copper, nitrogen and silicon. These alloys are known for their excellent strength at elevated temperatures and good corrosion resistance in a variety of corrosive environments.
INCOLOY alloy 800 is an alloy of nickel, iron and chromium. The alloy is capable of remaining stable and maintaining its austenitic structure even after long time exposures to high temperatures. Other characteristics of the alloy are good strength, and high resistance to oxidizing, reducing and aqueous environments. The standard forms in which this alloy is available are round, flats, forging stock, tube, plate, sheet, wire and strip.
This datasheet will look into the chemical composition, properties and applications of INCOLOY 800.
The chemical composition of INCOLOY alloy 800 is given in the following table.
|Minimum Order Quantity||50 Kg|
The principal alloying ingredients in aluminium / aluminum alloys include manganese, magnesium, copper, zinc and silicon. The market for aluminium / aluminum and its alloys is huge. About 22 million t is newly manufactured aluminium and 7 million t is recycled aluminium scrap.
Aluminium / aluminum 7020 alloy is a heat treatable wrought alloy. Zinc forms a major part of this alloy.
The following datasheet will provide more details about aluminium / aluminum 7020 alloy.
The following table shows the chemical composition of aluminium / aluminum 7020 alloy.
|Zirconium, Zr + Titanium, Ti||0.80 - 0.25|
|Chromium, Cr||0.10 - 0.35|
|Zirconium, Zr||0.080 - 0.20|
|Manganese, Mn||0.050 - 0.50|
|Other (each)||0.05 max|
|Other (total)||0.15 max|
The physical properties of aluminium / aluminum 7020 alloy are outlined in the following table.
|Density||2.78 g/cm³||0.100 lb/in³|
The mechanical properties of aluminium / aluminum 7020-T6 alloy are tabulated below.
Wire Gauge (SWG):
|Tensile strength (@thickness ≤100 mm/≤3.94 in)||≥ 350 MPa||≥ 50800 psi|
|Yield strength (@thickness ≤100 mm/≤3.94 in)||≥ 280 MPa||≥ 40600 psi|
|Elongation at break (@thickness ≤100 mm/≤3.94 in)||≥ 10%||≥ 10%|
Alloy 800HT (UNS N08811) Chemical Composition, %: