Prominent & Leading Manufacturer from Mumbai, we offer beryllium copper (uns c17200), beryllium copper / uns c17300 / din 2.1248 / alloy c17300 - pipe, beryllium copper / uns c17300 / din 2.1248 / alloy c17300 - wire, beryllium copper / uns c17200 / alloyc17200 / din 2.1247 - round bar, beryllium copper / uns c17200 / alloy c17200 / din 2.1247 - pipe and beryllium copper / uns c17300 / din 2.1248 / alloy c17300 - sheet.

Beryllium Copper (UNS C17200)

Beryllium Copper (UNS C17200)
  • Beryllium Copper (UNS C17200)
  • Beryllium Copper (UNS C17200)
Get Best Quote
Approx. Price: Rs 530 / KgGet Latest Price

Product Details:

Minimum Order Quantity50 Kg
MaterialCopper
Diameter>9mm, 0.02 - 1 mm, 7-9 mm, 1-3 mm, 5-7 mm, 3-5 mm
Gauge10-15, >25, 15-20, 0-5, 20-25, 5-10
Usage/ApplicationElectrical Industry
Thickness0.5 to 50mm Thick
Conductor TypeStranded
BrandFHA
ShapeRound
Length3 - 6 Meter
Round Wire0.5 to 50mm Dia
I Deal InNew Only
InsulationYes
Blue6000

UNS C17200 beryllium copper alloys are ductile and produced in mill hardened and heat treatable tempers. These alloys are used for all applications, which require high strength, stiffness and good conductivity. The tensile strength of C17200 copper is over 1380 MPa (200 ksi).

The following datasheet will explain about UNS C17200 beryllium copper alloys.

Chemical Composition

The following table shows the chemical composition of UNS C17200 copper.

Element

Content (%)

Cu

97.9

Be

1.9

Co

0.20

Physical Properties

The physical properties of UNS C17200 copper are given in the following table.

Properties

Metric

Imperial

Density (during age hardening, 2% max. decrease in length and 6% max. increase in density)

8.25 g/cm3

0.298 lb/in3

Melting point

866°C

1590°F

Mechanical Properties

The mechanical properties of UNS C17200 copper are tabulated below.

Properties

Metric

Imperial

Hardness, Rockwell B

80.0 - 85.0

80.0 - 85.0

Tensile strength, ultimate

1280 - 1480 MPa

186000 - 215000 psi

Tensile strength, yield

965 - 1205 MPa

140000 - 174800 psi

Elongation at break

15.0 - 30.0%

15.0 - 30.0%

Modulus of elasticity

125 - 130 GPa

18100 - 18900 ksi

Poissons ratio

0.300

0.300

Machinability (UNS C36000 (free-cutting brass) = 100%)

20%

20%

Shear modulus

50.0 GPa

7250 ksi

Request
Callback


Additional Information:

  • Item Code: BerylliumCopper_UNSC17200_AlloyC17200_Wire_RoundBar
  • Pay Mode Terms: L/C (Letter of Credit),T/T (Bank Transfer),D/P,D/A,Other
  • Port of Dispatch: Mumbai
  • Production Capacity: 500 MT per month
  • Delivery Time: 30 Day
  • Packaging Details: As Per Request..
Yes! I am Interested

Beryllium Copper / UNS C17300 / DIN 2.1248 / Alloy C17300 - Pipe

Beryllium Copper / UNS C17300 / DIN 2.1248 / Alloy C17300 - Pipe
  • Beryllium Copper / UNS C17300 / DIN 2.1248 / Alloy C17300 - Pipe
Get Best Quote
Approx. Price: Rs 1,420 / KgGet Latest Price

Product Details:

Minimum Order Quantity50 Kg
MaterialBeryllium Copper
BrandFHA
ShapePipe
GradeAlloy C17300
Uns No.C17300
I Deal InNew Only
Length25m
Outside Diameter500mm OD

Introduction

UNS C17300 beryllium copper alloys are heat treatable, ductile and can be mill hardened. They offer tensile strength of 1380 MPa (200 ksi). These steels are suitable for applications requiring good conductivity, high strength and stiffness.

This article will give an overview of UNS C17300 beryllium copper alloys.

Chemical Composition

The following table shows the chemical composition of UNS C17300 copper.

ElementContent (%)
Cu97.7
Be1.9
Co0.40
Physical Properties

The physical properties of UNS C17300 copper are given in the following table.

PropertiesMetricImperial
Density (during age hardening, 2% max. decrease in length and 6% max. increase in density)8.25 g/cm30.298 lb/in3
Melting point866°C1590°F
Mechanical Properties

The mechanical properties of UNS C17300 copper are tabulated below.

PropertiesMetricImperial
Hardness, Rockwell B80.0 - 85.080.0 - 85.0
Tensile strength, ultimate515 - 585 MPa74700 - 84800 psi
Tensile strength, yield275 - 345 MPa39900 - 50000 psi
Elongation at break15.0 - 30.0%15.0 - 30.0%
Modulus of elasticity125 - 130 GPa18100 - 18900 ksi
Poissons ratio0.3000.300
Machinability (UNS C36000 (free-cutting brass) = 100%)20%20%
Shear modulus50.0 GPa7250 ksi

Machinability

The machinability rate of C17300 copper alloys is 50%.

Welding

C17300 copper alloys can be welded using soldering, brazing, gas shielded arc welding, coated metal arc welding, spot welding, seam welding and butt welding. Oxyacetylene welding is not recommended for this type of alloys.

Forging

C17300 copper alloys are forged at temperatures ranging from 649 to 816°C (1200 to 1500°F).

Hot Working

C17300 copper alloys have good hot working property.

Cold Working

C17200 copper alloys have excellent cold working property.

Annealing

Annealing of C17200 copper alloys is performed at temperature ranging from 774 to 802°C (1425 to 1475°F).

Applications

The following are the major applications of UNS C17300 copper:

  • Electrical/electronic connectors
  • Current-carrying springs
  • Precision screw machined parts
  • Welding electrodes
  • Bearings
  • Plastic molds
  • Corrosion resistant components.
Request
Callback


Additional Information:

  • Item Code: BerylliumCopperUNSC17300AlloyC17300Pipe
  • Pay Mode Terms: L/C (Letter of Credit),T/T (Bank Transfer),D/P,D/A,Other
  • Port of Dispatch: Mumbai
  • Production Capacity: 500 MT per month
  • Delivery Time: 04 Day
  • Packaging Details: As Per Request..
Yes! I am Interested

Beryllium Copper / UNS C17300 / DIN 2.1248 / Alloy C17300 - Wire

Beryllium Copper / UNS C17300 / DIN 2.1248 / Alloy C17300 - Wire
  • Beryllium Copper / UNS C17300 / DIN 2.1248 / Alloy C17300 - Wire
Get Best Quote
Approx. Price: Rs 960 / KilogramGet Latest Price

Product Details:

Minimum Order Quantity50 Kilogram
Usage/ApplicationIndustrial
Thickness0.5 - 50mm
BrandFHA
ShapeRound
Packaging Size Kg0.3 - 2.0 Kgs
Packaging TypeAs Per Request
I Deal InNew Only
UNSC17300
DIN2.1248

Introduction

UNS C17300 beryllium copper alloys are heat treatable, ductile and can be mill hardened. They offer tensile strength of 1380 MPa (200 ksi). These steels are suitable for applications requiring good conductivity, high strength and stiffness.

This article will give an overview of UNS C17300 beryllium copper alloys.

 

Chemical Composition

The following table shows the chemical composition of UNS C17300 copper.

ElementContent (%)
Cu97.7
Be1.9
Co0.40
Physical Properties

The physical properties of UNS C17300 copper are given in the following table.

PropertiesMetricImperial
Density (during age hardening, 2% max. decrease in length and 6% max. increase in density)8.25 g/cm30.298 lb/in3
Melting point866°C1590°F
Mechanical Properties

The mechanical properties of UNS C17300 copper are tabulated below.

PropertiesMetricImperial
Hardness, Rockwell B80.0 - 85.080.0 - 85.0
Tensile strength, ultimate515 - 585 MPa74700 - 84800 psi
Tensile strength, yield275 - 345 MPa39900 - 50000 psi
Elongation at break15.0 - 30.0%15.0 - 30.0%
Modulus of elasticity125 - 130 GPa18100 - 18900 ksi
Poissons ratio0.3000.300
Machinability (UNS C36000 (free-cutting brass) = 100%)20%20%
Shear modulus50.0 GPa7250 ksi

Machinability

The machinability rate of C17300 copper alloys is 50%.

Welding

C17300 copper alloys can be welded using soldering, brazing, gas shielded arc welding, coated metal arc welding, spot welding, seam welding and butt welding. Oxyacetylene welding is not recommended for this type of alloys.

Forging

C17300 copper alloys are forged at temperatures ranging from 649 to 816°C (1200 to 1500°F).

Hot Working

C17300 copper alloys have good hot working property.

Cold Working

C17200 copper alloys have excellent cold working property.

Annealing

Annealing of C17200 copper alloys is performed at temperature ranging from 774 to 802°C (1425 to 1475°F).

Applications

The following are the major applications of UNS C17300 copper:

  • Electrical/electronic connectors
  • Current-carrying springs
  • Precision screw machined parts
  • Welding electrodes
  • Bearings
  • Plastic molds
  • Corrosion resistant components.
Request
Callback


Additional Information:

  • Item Code: BerylliumCopper_UNSC17300_DIN21248_AlloyC17300_Wire
  • Pay Mode Terms: L/C (Letter of Credit),T/T (Bank Transfer),D/P,D/A,Other
  • Port of Dispatch: Mumbai
  • Production Capacity: 500 MT per month
  • Delivery Time: 03 Day
  • Packaging Details: As Per Request..
Yes! I am Interested

Beryllium Copper / UNS C17200 / AlloyC17200 / DIN 2.1247 - Round Bar

Beryllium Copper / UNS C17200 / AlloyC17200 / DIN 2.1247 - Round Bar
  • Beryllium Copper / UNS C17200 / AlloyC17200 / DIN 2.1247 - Round Bar
Get Best Quote
Approx. Price: Rs 1,370 / KgGet Latest Price

Product Details:

Minimum Order Quantity50 Kg
ShapeRound
Material GradeAlloy C17200
Available GradesDin 2.1247
Single Piece Length3 - 6 Meter
GradeBeryllium Copper
Size5 to 500mm Dia
BrandFHA
I Deal InNew Only
UsageManufacturing, Household Repair, Construction
UNSC17200

UNS C17200 beryllium copper alloys are ductile and produced in mill hardened and heat treatable tempers. These alloys are used for all applications, which require high strength, stiffness and good conductivity. The tensile strength of C17200 copper is over 1380 MPa (200 ksi).

The following datasheet will explain about UNS C17200 beryllium copper alloys.

Chemical Composition

The following table shows the chemical composition of UNS C17200 copper.

Element

Content (%)

Cu

97.9

Be

1.9

Co

0.20

Physical Properties

The physical properties of UNS C17200 copper are given in the following table.

Properties

Metric

Imperial

Density (during age hardening, 2% max. decrease in length and 6% max. increase in density)

8.25 g/cm3

0.298 lb/in3

Melting point

866°C

1590°F

Mechanical Properties

The mechanical properties of UNS C17200 copper are tabulated below.

Properties

Metric

Imperial

Hardness, Rockwell B

80.0 - 85.0

80.0 - 85.0

Tensile strength, ultimate

1280 - 1480 MPa

186000 - 215000 psi

Tensile strength, yield

965 - 1205 MPa

140000 - 174800 psi

Elongation at break

15.0 - 30.0%

15.0 - 30.0%

Modulus of elasticity

125 - 130 GPa

18100 - 18900 ksi

Poissons ratio

0.300

0.300

Machinability (UNS C36000 (free-cutting brass) = 100%)

20%

20%

Shear modulus

50.0 GPa

7250 ksi


Machinability

The machinability rate of C17300 copper alloys is 50%.

Welding

C17300 copper alloys can be welded using soldering, brazing, gas shielded arc welding, coated metal arc welding, spot welding, seam welding and butt welding. Oxyacetylene welding is not recommended for this type of alloys.

Forging

C17300 copper alloys are forged at temperatures ranging from 649 to 816°C (1200 to 1500°F).

Hot Working

C17300 copper alloys have good hot working property.

Cold Working

C17200 copper alloys have excellent cold working property.

Annealing

Annealing of C17200 copper alloys is performed at temperature ranging from 774 to 802°C (1425 to 1475°F).

Applications

The following are the major applications of UNS C17300 copper:

  • Electrical/electronic connectors
  • Current-carrying springs
  • Precision screw machined parts
  • Welding electrodes
  • Bearings
  • Plastic molds
  • Corrosion resistant components.
Request
Callback


Additional Information:

  • Item Code: BerylliumCopperUNSC17200RoundBar
  • Pay Mode Terms: L/C (Letter of Credit),T/T (Bank Transfer),D/P,D/A,Other
  • Port of Dispatch: Mumbai
  • Production Capacity: 500 MT per month
  • Delivery Time: 04 Day
  • Packaging Details: As Per Request..
Yes! I am Interested

Beryllium Copper / UNS C17200 / Alloy C17200 / DIN 2.1247 - Pipe

Beryllium Copper / UNS C17200 / Alloy C17200 / DIN 2.1247 - Pipe
  • Beryllium Copper / UNS C17200 / Alloy C17200 / DIN 2.1247 - Pipe
Get Best Quote
Approx. Price: Rs 890 / KgGet Latest Price

Product Details:

Minimum Order Quantity50 Kg
MaterialBeryllium Copper
ShapeRound Bar
Surface FinishingSmooth
Thickness0.1 - 50mm Thick
Outside Diameter500mm OD
UNSC17200

UNS C17200 beryllium copper alloys are ductile and produced in mill hardened and heat treatable tempers. These alloys are used for all applications, which require high strength, stiffness and good conductivity. The tensile strength of C17200 copper is over 1380 MPa (200 ksi).

The following datasheet will explain about UNS C17200 beryllium copper alloys.

Chemical Composition

The following table shows the chemical composition of UNS C17200 copper.

Element

Content (%)

Cu

97.9

Be

1.9

Co

0.20

Physical Properties

The physical properties of UNS C17200 copper are given in the following table.

Properties

Metric

Imperial

Density (during age hardening, 2% max. decrease in length and 6% max. increase in density)

8.25 g/cm3

0.298 lb/in3

Melting point

866°C

1590°F

Mechanical Properties

The mechanical properties of UNS C17200 copper are tabulated below.

Properties

Metric

Imperial

Hardness, Rockwell B

80.0 - 85.0

80.0 - 85.0

Tensile strength, ultimate

1280 - 1480 MPa

186000 - 215000 psi

Tensile strength, yield

965 - 1205 MPa

140000 - 174800 psi

Elongation at break

15.0 - 30.0%

15.0 - 30.0%

Modulus of elasticity

125 - 130 GPa

18100 - 18900 ksi

Poissons ratio

0.300

0.300

Machinability (UNS C36000 (free-cutting brass) = 100%)

20%

20%

Shear modulus

50.0 GPa

7250 ksi

Machinability

The machinability rate of C17300 copper alloys is 50%.

Welding

C17300 copper alloys can be welded using soldering, brazing, gas shielded arc welding, coated metal arc welding, spot welding, seam welding and butt welding. Oxyacetylene welding is not recommended for this type of alloys.

Forging

C17300 copper alloys are forged at temperatures ranging from 649 to 816°C (1200 to 1500°F).

Hot Working

C17300 copper alloys have good hot working property.

Cold Working

C17200 copper alloys have excellent cold working property.

Annealing

Annealing of C17200 copper alloys is performed at temperature ranging from 774 to 802°C (1425 to 1475°F).

Applications

The following are the major applications of UNS C17300 copper:

  • Electrical/electronic connectors
  • Current-carrying springs
  • Precision screw machined parts
  • Welding electrodes
  • Bearings
  • Plastic molds
  • Corrosion resistant components.
Request
Callback


Additional Information:

  • Item Code: BerylliumCopper_UNSC17200_AlloyC17200_Pipe
  • Pay Mode Terms: L/C (Letter of Credit),T/T (Bank Transfer),D/P,D/A,Other
  • Port of Dispatch: Mumbai
  • Production Capacity: 500 MT per month
  • Delivery Time: 04 Day
  • Packaging Details: As Per Request..
Yes! I am Interested

Beryllium Copper / UNS C17300 / DIN 2.1248 / Alloy C17300 - Sheet

Beryllium Copper / UNS C17300 / DIN 2.1248 / Alloy C17300 - Sheet
  • Beryllium Copper / UNS C17300 / DIN 2.1248 / Alloy C17300 - Sheet
Get Best Quote
Approx. Price: Rs 1,480 / KgGet Latest Price

Product Details:

Minimum Order Quantity10 Kg
MaterialBeryllium Copper
Size3 - 6 Meter
ShapeSheet
GradeC17300
BrandFHA
I Deal InNew Only
Sheet Size (feet X feet)0.5 - 50mm Thick
Surface TreatmentCoated,Painted,Hot Rolled,Cold Rolled
UNSC17300

UNS C17300 beryllium copper alloys are heat treatable, ductile and can be mill hardened. They offer tensile strength of 1380 MPa (200 ksi). These steels are suitable for applications requiring good conductivity, high strength and stiffness.

This article will give an overview of UNS C17300 beryllium copper alloys.

Chemical Composition
The following table shows the chemical composition of UNS C17300 copper.
ElementContent (%)
Cu97.7
Be1.9
Co0.40
Physical Properties

The physical properties of UNS C17300 copper are given in the following table.

PropertiesMetricImperial
Density (during age hardening, 2% max. decrease in length and 6% max. increase in density)8.25 g/cm30.298 lb/in3
Melting point866°C1590°F
Mechanical Properties

The mechanical properties of UNS C17300 copper are tabulated below.

PropertiesMetricImperial
Hardness, Rockwell B80.0 - 85.080.0 - 85.0
Tensile strength, ultimate515 - 585 MPa74700 - 84800 psi
Tensile strength, yield275 - 345 MPa39900 - 50000 psi
Elongation at break15.0 - 30.0%15.0 - 30.0%
Modulus of elasticity125 - 130 GPa18100 - 18900 ksi
Poissons ratio0.3000.300
Machinability (UNS C36000 (free-cutting brass) = 100%)20%20%
Shear modulus50.0 GPa7250 ksi
Request
Callback


Additional Information:

  • Item Code: BerylliumCopperUNSC17300DIN21248AlloyC17300Sheet
  • Pay Mode Terms: L/C (Letter of Credit),T/T (Bank Transfer),D/P,D/A,Other
  • Port of Dispatch: Mumbai
  • Production Capacity: 500 MT per month
  • Delivery Time: 03 Day
  • Packaging Details: As Per Request..
Yes! I am Interested

Beryllium Copper / UNS C17300 / DIN 2.1248 - Round Bar

Beryllium Copper / UNS C17300 / DIN 2.1248 - Round Bar
  • Beryllium Copper / UNS C17300 / DIN 2.1248 - Round Bar
Get Best Quote
Approx. Price: Rs 1,425 / KgGet Latest Price

Product Details:

Minimum Order Quantity500 Kg
GradeC17300
ShapeRound
Material GradeBeryllium Copper
I Deal InNew Only
BrandFHA
Size5 To 500mm Dia
Single Piece Length3 - 6 Meter
UsageManufacturing,Construction,Household Repair
UNSC17300

Introduction

UNS C17300 beryllium copper alloys are heat treatable, ductile and can be mill hardened. They offer tensile strength of 1380 MPa (200 ksi). These steels are suitable for applications requiring good conductivity, high strength and stiffness.

This article will give an overview of UNS C17300 beryllium copper alloys.

Chemical Composition

The following table shows the chemical composition of UNS C17300 copper.

ElementContent (%)
Cu97.7
Be1.9
Co0.40
Physical Properties

The physical properties of UNS C17300 copper are given in the following table.

PropertiesMetricImperial
Density (during age hardening, 2% max. decrease in length and 6% max. increase in density)8.25 g/cm30.298 lb/in3
Melting point866°C1590°F
Mechanical Properties

The mechanical properties of UNS C17300 copper are tabulated below.

PropertiesMetricImperial
Hardness, Rockwell B80.0 - 85.080.0 - 85.0
Tensile strength, ultimate515 - 585 MPa74700 - 84800 psi
Tensile strength, yield275 - 345 MPa39900 - 50000 psi
Elongation at break15.0 - 30.0%15.0 - 30.0%
Modulus of elasticity125 - 130 GPa18100 - 18900 ksi
Poissons ratio0.3000.300
Machinability (UNS C36000 (free-cutting brass) = 100%)20%20%
Shear modulus50.0 GPa7250 ksi

Machinability

The machinability rate of C17300 copper alloys is 50%.

Welding

C17300 copper alloys can be welded using soldering, brazing, gas shielded arc welding, coated metal arc welding, spot welding, seam welding and butt welding. Oxyacetylene welding is not recommended for this type of alloys.

Forging

C17300 copper alloys are forged at temperatures ranging from 649 to 816°C (1200 to 1500°F).

Hot Working

C17300 copper alloys have good hot working property.

Cold Working

C17200 copper alloys have excellent cold working property.

Annealing

Annealing of C17200 copper alloys is performed at temperature ranging from 774 to 802°C (1425 to 1475°F).

Applications

The following are the major applications of UNS C17300 copper:

  • Electrical/electronic connectors
  • Current-carrying springs
  • Precision screw machined parts
  • Welding electrodes
  • Bearings
  • Plastic molds
  • Corrosion resistant components.
Request
Callback


Additional Information:

  • Item Code: BerylliumCopper_UNSC17300_DIN21248_RoundBar
  • Pay Mode Terms: L/C (Letter of Credit),T/T (Bank Transfer),D/P,D/A,Other
  • Port of Dispatch: Mumbai
  • Production Capacity: 500 MT per month
  • Delivery Time: 02 Day
  • Packaging Details: As Per Request..
Yes! I am Interested

Beryllium Copper / UNS C17200 / Alloy C17200 / DIN 2.1247 - Wire

Beryllium Copper / UNS C17200 / Alloy C17200 / DIN 2.1247 - Wire
  • Beryllium Copper / UNS C17200 / Alloy C17200 / DIN 2.1247 - Wire
  • Beryllium Copper / UNS C17200 / Alloy C17200 / DIN 2.1247 - Wire
Get Best Quote
Approx. Price: Rs 780 / KgGet Latest Price

Product Details:

Minimum Order Quantity05 Kg
MaterialBeryllium Copper
ShapeWire
Size0.5 - 50mm Dia
I Deal InNew Only
Thickness0.04 - 5mm
GradeAlloy C12700
UNSC12700
DIN2.1247

UNS C17200 beryllium copper alloys are ductile and produced in mill hardened and heat treatable tempers. These alloys are used for all applications, which require high strength, stiffness and good conductivity. The tensile strength of C17200 copper is over 1380 MPa (200 ksi).

The following datasheet will explain about UNS C17200 beryllium copper alloys.

Chemical Composition

The following table shows the chemical composition of UNS C17200 copper.

Element

Content (%)

Cu

97.9

Be

1.9

Co

0.20

Physical Properties

The physical properties of UNS C17200 copper are given in the following table.

Properties

Metric

Imperial

Density (during age hardening, 2% max. decrease in length and 6% max. increase in density)

8.25 g/cm3

0.298 lb/in3

Melting point

866°C

1590°F

Mechanical Properties

The mechanical properties of UNS C17200 copper are tabulated below.

Properties

Metric

Imperial

Hardness, Rockwell B

80.0 - 85.0

80.0 - 85.0

Tensile strength, ultimate

1280 - 1480 MPa

186000 - 215000 psi

Tensile strength, yield

965 - 1205 MPa

140000 - 174800 psi

Elongation at break

15.0 - 30.0%

15.0 - 30.0%

Modulus of elasticity

125 - 130 GPa

18100 - 18900 ksi

Poissons ratio

0.300

0.300

Machinability (UNS C36000 (free-cutting brass) = 100%)

20%

20%

Shear modulus

50.0 GPa

7250 ksi


Machinability

The machinability rate of C17300 copper alloys is 50%.

Welding

C17300 copper alloys can be welded using soldering, brazing, gas shielded arc welding, coated metal arc welding, spot welding, seam welding and butt welding. Oxyacetylene welding is not recommended for this type of alloys.

Forging

C17300 copper alloys are forged at temperatures ranging from 649 to 816°C (1200 to 1500°F).

Hot Working

C17300 copper alloys have good hot working property.

Cold Working

C17200 copper alloys have excellent cold working property.

Annealing

Annealing of C17200 copper alloys is performed at temperature ranging from 774 to 802°C (1425 to 1475°F).

Applications

The following are the major applications of UNS C17300 copper:

  • Electrical/electronic connectors
  • Current-carrying springs
  • Precision screw machined parts
  • Welding electrodes
  • Bearings
  • Plastic molds
  • Corrosion resistant components.
Request
Callback


Additional Information:

  • Item Code: BerylliumCopper_UNSC17200_AlloyC17200
  • Production Capacity: 50 MT Per Month
  • Delivery Time: 02 Days
  • Packaging Details: As Per Request....
Yes! I am Interested

Beryllium Copper / UNS C17200 / Alloy C17200 / DIN 2.1247 - Sheet

Beryllium Copper / UNS C17200 / Alloy C17200 / DIN 2.1247 - Sheet
  • Beryllium Copper / UNS C17200 / Alloy C17200 / DIN 2.1247 - Sheet
Get Best Quote
Approx. Price: Rs 720 / KgGet Latest Price

Product Details:

Minimum Order Quantity50 Kg
GradeAlloy C17200
Beryllium CopperDIN 2.1247
MaterialBeryllium Copper
Size3 - 6 Meter
TypeSheet
Thickness0.2mm - 50mm
UNSC17200
FinishSmooth

UNS C17200 beryllium copper alloys are ductile and produced in mill hardened and heat treatable tempers. These alloys are used for all applications, which require high strength, stiffness and good conductivity. The tensile strength of C17200 copper is over 1380 MPa (200 ksi).

The following datasheet will explain about UNS C17200 beryllium copper alloys.

Chemical Composition

The following table shows the chemical composition of UNS C17200 copper.

Element

Content (%)

Cu

97.9

Be

1.9

Co

0.20

Physical Properties

The physical properties of UNS C17200 copper are given in the following table.

Properties

Metric

Imperial

Density (during age hardening, 2% max. decrease in length and 6% max. increase in density)

8.25 g/cm3

0.298 lb/in3

Melting point

866°C

1590°F

Mechanical Properties

The mechanical properties of UNS C17200 copper are tabulated below.

Properties

Metric

Imperial

Hardness, Rockwell B

80.0 - 85.0

80.0 - 85.0

Tensile strength, ultimate

1280 - 1480 MPa

186000 - 215000 psi

Tensile strength, yield

965 - 1205 MPa

140000 - 174800 psi

Elongation at break

15.0 - 30.0%

15.0 - 30.0%

Modulus of elasticity

125 - 130 GPa

18100 - 18900 ksi

Poissons ratio

0.300

0.300

Machinability (UNS C36000 (free-cutting brass) = 100%)

20%

20%

Shear modulus

50.0 GPa

7250 ksi


Machinability

The machinability rate of C17300 copper alloys is 50%.

Welding

C17300 copper alloys can be welded using soldering, brazing, gas shielded arc welding, coated metal arc welding, spot welding, seam welding and butt welding. Oxyacetylene welding is not recommended for this type of alloys.

Forging

C17300 copper alloys are forged at temperatures ranging from 649 to 816°C (1200 to 1500°F).

Hot Working

C17300 copper alloys have good hot working property.

Cold Working

C17200 copper alloys have excellent cold working property.

Annealing

Annealing of C17200 copper alloys is performed at temperature ranging from 774 to 802°C (1425 to 1475°F).

Applications

The following are the major applications of UNS C17300 copper:

  • Electrical/electronic connectors
  • Current-carrying springs
  • Precision screw machined parts
  • Welding electrodes
  • Bearings
  • Plastic molds
  • Corrosion resistant components.
Request
Callback


Additional Information:

  • Item Code: BerylliumCopper_UNSC17200_Sheet
  • Production Capacity: 50 MT Per Month
  • Delivery Time: 02 Days
  • Packaging Details: As Per Request..
Yes! I am Interested
X

Explore More Product



Reach Us
Anil Gupta (Sales Manager)
FountainHead Alloys
B-12A, Flox Chambers, Tata Road No. 1, Opera House
Mumbai - 400004, Maharashtra, India



Call Us


Send E-mailSend SMS