Aluminium Alloys

Pure aluminium is relatively soft. To overcome this, the metal can be alloyed with other metals (alloying elements). Most of the aluminium reaching the marketplace has been alloyed with at least one other element.Based on the type of alloying element, the aluminium alloys are divided into 8 groups  
 Alloy code
 1xxx Series
 2xxx Series
 3xxx Series
 4xxx Series
 5xxx Series The alloying element is magnesium. Alloys of this series are moderate in strength (200 – 350 MPa). The strength is achieved by the heat treatment processing or forming. Alloys of this series have excellent resistance to corrosion in aggressive atmosphere and seawater.
 6xxx Series The alloying elements are magnesium and silicon. Alloys of this series are moderate in strength (200 – 350 MPa). The strength is achieved by the heat treatment processing or forming. Alloys of 6xxx series can be easily anodized.
 7xxx Series The alloying element is zinc. Alloys of this series have the highest strength among all series. The tensile strengths ranging between 450 – 500 MPa may exceed 600 MPa in some cases. These alloys prone to stress corrosion, especially when welded.
 8xxx Series The alloying element is other than for the other series (including lithium).

Aluminium Alloys 6005 62400 C51S Wire

Aluminium Alloys 6005 62400 C51S Wire
  • Aluminium Alloys 6005 62400 C51S Wire
Get Best Quote
Approx. Price: Rs 190 / KilogramGet Latest Price

Product Details:

Minimum Order Quantity50 Kilogram
MaterialAluminum Alloy
Usage/ApplicationConstruction
BrandFHA
Length100 m
FormWire
Packaging TypeRoll
GradeAl 6005 62400 C51S

Aluminium alloy 6005i s a medium strength, heat treatable alloy with excellent corrosion resistance.


Alloy 6005 has properties between those of alloys 6061 and 6082 and can sometimes be used interchangeably with these alloys but 6005/6005A has better extrusion characteristics. It has a better mill surface finish, but it is difficult to produce thin-wall complicated shapes in 6005/6005A. 6005 has very good bending properties.


Chemical Composition:

Chemical composition for aluminium alloy 6005

Element

% Present

Si

0.5-0.9

Fe

0.0-0.35

Cu

0.0-0.3

Mn

0.0-0.5

Mg

0.4-0.7

Zn

0.0-0.2

Ti

0.0-0.1

Cr

0.0-0.3

Mn+Cr

0.12-0.5

Al

Balance


Mechanical Properties:

Mechanical properties for aluminium alloy 6005 T6

BS EN 755-2:2008
Rod Bar
up to 25mm Dia. A/F

Property

Value

Proof Stress

225 Min MPa

Tensile Strength

270 Min MPa

Elongation A50 mm

8 %

Shear Strength

205 MPa

Hardness Brinell

90 HB

Elongation A

10 Min %

Request
Callback
Yes! I am Interested

Aluminium Alloys 7039 D74S 74530 Round Bar

Aluminium Alloys 7039 D74S 74530 Round Bar
  • Aluminium Alloys 7039 D74S 74530 Round Bar
Get Best Quote
Approx. Price: Rs 290 / KilogramGet Latest Price

Product Details:

Minimum Order Quantity50 Kilogram
ShapeRound
Usage/ApplicationConstruction
MaterialAluminum Alloy
GradeAl 7039 D74S 74530
Single Piece Length6 meter
BrandFHA
Diameter350 mm

Aluminium / aluminum is one of the lightest available commercial metals with a density approximately one-third that of steel or copper. It can be easily fabricated into many forms such as foil, sheets, rod, tube, geometric shapes, and wire.


Aluminium / aluminum 7039 alloy is a heat treatable wrought alloy. The following datasheet will provide more details about aluminium / aluminum 7039 alloy.


Chemical Composition:

The following table shows the chemical composition of aluminium / aluminum 7039 alloy.

ElementContent (%)
Zinc, Zn 3.5 - 4.5
Magnesium, Mg 2.3 - 3.3
Silicon, Si 0.3 max
Iron, Fe 0.4 max
Chromium, Cr 0.15 - 0.25
Manganese, Mn 0.1 - 0.4
Copper, Cu 0.1 max
Titanium, Ti 0.1 max
Remainder (total) 0.15 max
Aluminum, Al Remainder

Physical Properties:

The physical properties of aluminium / aluminum 7039 alloy are outlined in the following table.

PropertiesMetricImperial
Density 2.74 g/cm³ 0.0990 lb/in³
Melting point 482-638°C 900-1180 °F

Mechanical Properties:

The mechanical properties of aluminium / aluminum 7039-T64 alloy are tabulated below.

PropertiesMetricImperial
Tensile strength (@diameter 12.7 mm/0.500 in) 450 MPa 65300 psi
Yield strength (@diameter 12.7 mm/0.500 in) 380 MPa 55100 psi
Elongation at break (@diameter 12.7 mm/0.500 in) 13% 13%
Elastic modulus 69.6 GPa 10100 ksi
Shear strength 255 MPa 37000 psi
Hardness, Brinell (@load 500 kg; thickness 10.0 mm/1100 lb;0.394 in) 133 133
Hardness, Knoop (converted from Brinell hardness value) 167 167
Hardness, Rockwell A (converted from Brinell hardness value) 50 50
Hardness, Rockwell B (converted from brinell hardness value) 81 81
Hardness, Vickers (converted from Brinell hardness value) 153 153
Request
Callback
Yes! I am Interested

Aluminum Alloy 5005 Round Bar

Aluminum Alloy 5005 Round Bar
  • Aluminum Alloy 5005 Round Bar
Get Best Quote
Approx. Price: Rs 310 / KilogramGet Latest Price

Product Details:

Minimum Order Quantity50 Kilogram
GradeAl 5005
Usage/ApplicationConstruction
BrandFHA
Length18 meter
Diameter350 mm
MaterialAluminum

Aluminium alloy 5005 contains nominally 0.8% magnesium. It has medium strength, good weldability, and good corrosion resistance in marine atmospheres. It also has the low density and excellent thermal conductivity common to all aluminium alloys. It is the most commonly used grade of aluminium in sheet and plate form.


Aluminium alloy 5005 is a lean aluminium magnesium alloy which can be hardened by cold work: it is not heat treatable to higher strength.


Austral Wright Metals can supply this alloy as plate, sheet and strip. See Austral Wright Metals Catalogue for normal stock sizes and tempers.


Corrosion Resistance 5005 has the same high resistance to general corrosion as other non heat treatable aluminium alloys. It also has the higher resistance to slightly alkaline conditions common to the 5000 series alloys. The atmospheric corrosion resistance of 5005 is similar to that of 3003.


When anodised to improve corrosion resistance, the film on 5005 is clearer than on 3003, and gives better colour match with 6063 architectural extrusions.


The corrosion resistance of aluminium alloys relies on a protective surface oxide film, which when damaged is readily repaired by the rapid reaction between aluminium and oxygen. However, the high reactivity of the base metal can give rapid corrosion if the film cannot be repaired, so aluminium alloys are not suitable for use with reducing media.


Since aluminium is a reactive metal, it may corrode more quickly when in electrical contact with most other metals. The prediction of galvanic corrosion is complex, please consult Austral Wright Metals for specific advice.


Typical Applications of aluminium alloy 5005 include:

  • Architectural applications
  • General sheet metal work
  • High strength foil.

Chemical composition of Aluminium 5005.

Element

%

Element

%

Aluminium

Balance

Manganese

0.20 max

Magnesium

0.50 – 1.10

Chromium

0.10 max

Silicon

0.30max

Zinc

0.25 max

Iron

0.07 max

Others, each

0.05 max

Copper

0.20 max

Others, total

0.15 max

Request
Callback
Yes! I am Interested

Aluminum Alloys 6061 Plate

Aluminum Alloys 6061 Plate
  • Aluminum Alloys 6061 Plate
Ask For Price
Product Price :Get Latest Price

Product Details:

MaterialAluminum Alloys
ColorSilver
Material GradeAl 6061 Al-Mg-Si Cu
Length6000 mm
Thickness50 mm
FinishBright
BrandFHA
ApplicationConstruction

Aluminium alloy 6061 is one of the most extensively used of the 6000 series aluminium alloys. It is a versatile heat treatable extruded alloy with medium to high strength capabilities.


Composition:

Typical composition of aluminium alloy 6061

Component

Amount (wt.%)

Aluminium

Balance

Magnesium

0.8-1.2

Silicon

0.4 – 0.8

Iron

Max. 0.7

Copper

0.15-0.40

Zinc

Max. 0.25

Titanium

Max. 0.15

Manganese

Max. 0.15

Chromium

0.04-0.35

Others

0.05

 

Key Features:

Typical properties of aluminium alloy 6061 include:

  • Medium to high strength
  • Good toughness
  • Good surface finish
  • Excellent corrosion resistance to atmospheric conditions
  • Good corrosion resistance to sea water
  • Can be anodized
  • Good weldability and brazability
  • Good workability
  • Widely available


Mechanical Properties:

emper

Ultimate Tensile Strength (MPa)

0.2% Proof Stress (MPa)

Brinell Hardness (500kg load, 10mm ball)

Elongation 50mm dia (%)

0

110-152

65-110

30-33

14-16

T1

180

95-96

 

16

T4

179 min

110 min

 

 

T6

260-310

240-276

95-97

9-13

 

Request
Callback
Yes! I am Interested

Aluminium Alloys 6066 64423 H11 C62S Wire

Aluminium Alloys 6066 64423 H11 C62S Wire
  • Aluminium Alloys 6066 64423 H11 C62S Wire
Ask For Price
Product Price :Get Latest Price

Product Details:

MaterialAluminum Alloy
Usage/ApplicationConstruction
BrandFHA
ShapeRound
Length100 m
FormWire
Packaging TypeRoll
GradeAl 6066 64423 H11 C62S

Aluminium / Aluminum alloys have good corrosion resistance. They tend to lose some of their strength when subjected to high temperatures. However, their strength can be increased when exposed to subzero temperatures.


The following datasheet gives an overview of Aluminium / Aluminum 6066 alloy.


Chemical Composition:

The following table shows the chemical composition of Aluminium / Aluminum 6066 alloy.

Element

Content (%)

Aluminium / Aluminum, Al

95.7

Silicon, Si

1.40

Magnesium, Mg

1.10

Copper, Cu

1

Manganese, Mn

0.8


Physical Properties:

Properties

Metric

Imperial

Density

2.6-2.8 g/cm3

0.0939- 0.101 lb/in3


Mechanical Properties:

The mechanical properties of Aluminium / Aluminum 6066 alloy are outlined in the following table.

Properties

Metric

Imperial

Tensile strength

150 MPa

21755 psi

Yield strength

83 MPa

12038 psi

Shear strength

97 MPa

14069 psi

Fatigue strength

110 MPa

15954 psi

Elastic modulus

70-80 GPa

10153-11603 ksi

Poisson's ratio

0.33

0.33

Hardness

43

43


Wire Gauge (SWG):

  • 8 SWG, 10 SWG, 20 SWG, 30 SWG, 32 SWG


Certification:

  • BS ,DIN ,IEC, NFC, CSA

Request
Callback
Yes! I am Interested

Aluminium Alloys 6005 62400 C51S Sheet

Aluminium Alloys 6005 62400 C51S Sheet
  • Aluminium Alloys 6005 62400 C51S Sheet
Get Best Quote
Approx. Price: Rs 520 / KilogramGet Latest Price

Product Details:

Minimum Order Quantity50 Kilogram
ShapeRectangular
Grade6005/6005A
Thickness45 mm
BrandFHA
Tolerance-0.00mm/+5.00mm
MaterialAluminium
Length24 meter

Aluminium alloy 6005i s a medium strength, heat treatable alloy with excellent corrosion resistance.


Alloy 6005 has properties between those of alloys 6061 and 6082 and can sometimes be used interchangeably with these alloys but 6005/6005A has better extrusion characteristics. It has a better mill surface finish, but it is difficult to produce thin-wall complicated shapes in 6005/6005A.

6005 has very good bending properties.


Chemical Composition:

Chemical composition for aluminium alloy 6005

Element

% Present

Si

0.5-0.9

Fe

0.0-0.35

Cu

0.0-0.3

Mn

0.0-0.5

Mg

0.4-0.7

Zn

0.0-0.2

Ti

0.0-0.1

Cr

0.0-0.3

Mn+Cr

0.12-0.5

Al

Balance

Properties

Mechanical Properties:

Mechanical properties for aluminium alloy 6005 T6

BS EN 755-2:2008
Rod Bar
up to 25mm Dia. A/F

Property

Value

Proof Stress

225 Min MPa

Tensile Strength

270 Min MPa

Elongation A50 mm

8 %

Shear Strength

205 MPa

Hardness Brinell

90 HB

Elongation A

10 Min %

Request
Callback
Yes! I am Interested

Aluminium Alloys 6101 63401 91E D50S E.Al.Mg.Si 0.5 Sheet

Aluminium Alloys 6101 63401 91E D50S E.Al.Mg.Si 0.5 Sheet
  • Aluminium Alloys 6101 63401 91E D50S E.Al.Mg.Si 0.5 Sheet
Get Best Quote
Approx. Price: Rs 295 / KilogramGet Latest Price

Product Details:

Minimum Order Quantity50 Kilogram
ShapeRectangular
TypePlate
Material GradeAl 6101 63401 91E D50S E.Al.Mg.Si 0.5
BrandFHA
Tolerance-0.00mm/+5.00mm
MaterialAluminum Alloy
Length6000 mm

Aluminium / Aluminum alloys have good corrosion resistance. The strength of these alloys can be reduced when they are exposed to high temperatures. However, their strength can be increased at subzero temperatures. Aluminium / Aluminum 6101 alloy has good mechanical strength and high electrical conductivity.


The following datasheet will discuss in detail about Aluminium / Aluminum 6101 alloy.


Chemical Composition:


  • Unit Length : 6 m ,12 m , 18 m , 24m
  • Shape : Round Square , Rectangular, Oval
  • Surface Finish :Anodized, Brushed , Mill Finished ,Finished Polished

The following table shows the chemical composition of Aluminium / Aluminum 6101 alloy.

ElementContent (%)
Aluminium / Aluminum, Al 98.9
Magnesium, Mg 0.60
Silicon, Si 0.50

Physical Properties:

The physical properties of Aluminium / Aluminum 6101 alloy are given in the following table.

PropertiesMetricImperial
Density 2.7 g/cm3 0.0975 lb/in3
Melting point 588°C 1090°F

Mechanical Properties:

The mechanical properties of Aluminium / Aluminum 6101 alloy are tabulated below.

PropertiesMetricImperial
Tensile strength 97 MPa 14069 psi
Yield strength 76 MPa 11023 psi
Elastic modulus 70-80 GPa 10153-11603 ksi
Poisson's ratio 0.33 0.33

Thermal Properties:

The thermal properties of Aluminium / Aluminum 6101 alloy are given in the following table.

PropertiesConditions
T (ºC)Treatment
Thermal expansion 23 (10-6/ºC) 20-100 -
Thermal conductivity 218 W/mK 25 T6
Request
Callback
Yes! I am Interested

Aluminum Alloys 8011 40800/Al-Fe-Si Tube

Aluminum Alloys 8011 40800/Al-Fe-Si Tube
  • Aluminum Alloys 8011 40800/Al-Fe-Si Tube
Get Best Quote
Approx. Price: Rs 125 / KgGet Latest Price

Product Details:

Unit Length12 m
GradeAl 8011
Usage/ApplicationChemical Handling
Size/Diameter4 inch
Thickness50 mm
MaterialAluminum Alloys
ShapeRound
Surface FinishAnodized
Surface FinishingPolish
EndPlain End
BrandFHA

Apart from iron, aluminium / aluminum is currently the next most widely used metal in the world. This is due to the fact that aluminium / aluminum has a unique combination of attractive properties. Properties such as its low weight, corrosion resistance, and easy maintenance of final product, have ensured that this metal and its alloys will be in use for a very long time.


Aluminium / aluminum 8011 alloy is a wrought alloy. The following datasheet will provide more details about aluminium / aluminum 8011 alloy.


Chemical Composition:

The following table shows the chemical composition of aluminium / aluminum 8011 alloy.

ElementContent (%)
Aluminum, Al 97.3 - 98.9
Iron, Fe 0.60 - 1
Silicon, Si 0.50 - 0.90
Manganese, Mn ≤ 0.20
Zinc, Zn ≤ 0.10
Copper, Cu ≤ 0.10
Titanium, Ti ≤ 0.080
Chromium, Cr ≤ 0.050
Magnesium, Mg ≤ 0.050
Remainder (each) ≤ 0.050
Remainder (total) ≤ 0.15
Request
Callback
Yes! I am Interested

Aluminum Alloys 8011 40800 Al-Fe-Si Wire

Aluminum Alloys 8011 40800 Al-Fe-Si Wire
  • Aluminum Alloys 8011 40800 Al-Fe-Si Wire
Get Best Quote
Approx. Price: Rs 215 / KilogramGet Latest Price

Product Details:

Minimum Order Quantity50 Kilogram
MaterialAluminum Alloy
Usage/ApplicationConstruction
BrandFHA
ShapeRound
Length500 m
Packaging TypeRoll
GradeAl 8011 40800 Al-Fe-Si

Apart from iron, aluminium / aluminum is currently the next most widely used metal in the world. This is due to the fact that aluminium / aluminum has a unique combination of attractive properties. Properties such as its low weight, corrosion resistance, and easy maintenance of final product, have ensured that this metal and its alloys will be in use for a very long time.


Aluminium / aluminum 8011 alloy is a wrought alloy. The following datasheet will provide more details about aluminium / aluminum 8011 alloy.


Chemical Composition:

The following table shows the chemical composition of aluminium / aluminum 8011 alloy.

ElementContent (%)
Aluminum, Al 97.3 - 98.9
Iron, Fe 0.60 - 1
Silicon, Si 0.50 - 0.90
Manganese, Mn ≤ 0.20
Zinc, Zn ≤ 0.10
Copper, Cu ≤ 0.10
Titanium, Ti ≤ 0.080
Chromium, Cr ≤ 0.050
Magnesium, Mg ≤ 0.050
Remainder (each) ≤ 0.050
Remainder (total) ≤ 0.15
Request
Callback
Yes! I am Interested

Aluminum Alloys 6082 Al-Mg-Si 1 Forged Block

Aluminum Alloys 6082 Al-Mg-Si 1 Forged Block
    Get Best Quote
    Approx. Price: Rs 302 / KgGet Latest Price

    Product Details:

    Minimum Order Quantity50 Kg
    GradeAl 6082 Al-Mg-Si 1
    ShapeRectangular
    ColorGray
    ApplicationHydraulic Pipe, Gas Pipe, Structure Pipe
    BrandFHA
    MaterialAluminum Alloys
    Thread Size500 mm

    Aluminium alloy 6082 is a medium strength alloy with excellent corrosion resistance. It has the highest strength of the 6000 series alloys. Alloy 6082 is known as a structural alloy. In plate form, Aluminium alloy 6082is the alloy most commonly used for machining.


    As a relatively new alloy, the higher strength of Aluminium alloy 6082 has seen it replace 6061 in many applications. The addition of a large amount of manganese controls the grain structure which in turn results in a stronger alloy.


    In the T6 and T651 temper, Aluminium alloy 6082 machines well and produces tight coils of swarf when chip breakers are used.


    Chemical Composition of Aluminium alloy 6082

    Chemical composition for aluminium alloy 6082

    Element

    % Present

    Si

    0.7-1.3

    Fe

    0.0-0.5

    Cu

    0.0-0.1

    Mn

    0.4-1.0

    Mg

    0.6-1.2

    Zn

    0.0-0.2

    Ti

    0.0-0.1

    Cr

    0.0-0.25

    Al

    Balance


    Properties of Aluminium alloy 6082

    Mechanical properties for aluminium alloy 6082 Soft O

    BS EN 485-2:2008
    Sheet
    0.4mm to 6.00mm

    Property

    Value

    Proof Stress

    85 Max MPa

    Tensile Strength

    150 Max MPa

    Hardness Brinell

    40 HB

    Request
    Callback
    Get Best Quote
    Yes! I am Interested
    X

    Explore More Products

    View All Products




    Reach Us
    Anil Gupta (Sales Manager)
    Fountainhead Alloys
    B-12A, Flox Chambers, Tata Road No. 1, Opera House
    Mumbai - 400004, Maharashtra, India
    Get Directions


    Call Us


    Send E-mail