Product Details:
| Minimum Order Quantity | 50 Kg |
| Material | Aluminum Alloy |
| Usage/Application | Construction |
| Brand | FHA |
| Length | 100 m |
| Packaging Type | Roll |
| Grade | Al 7039 |
| Standard | D74S 74530 |
Aluminium / aluminum is one of the lightest available commercial metals with a density approximately one-third that of steel or copper. It can be easily fabricated into many forms such as foil, sheets, rod, tube, geometric shapes, and wire.
Aluminium / aluminum 7039 alloy is a heat treatable wrought alloy. The following datasheet will provide more details about aluminium / aluminum 7039 alloy.
The following table shows the chemical composition of aluminium / aluminum 7039 alloy.
| Element | Content (%) |
|---|---|
| Zinc, Zn | 3.5 - 4.5 |
| Magnesium, Mg | 2.3 - 3.3 |
| Silicon, Si | 0.3 max |
| Iron, Fe | 0.4 max |
| Chromium, Cr | 0.15 - 0.25 |
| Manganese, Mn | 0.1 - 0.4 |
| Copper, Cu | 0.1 max |
| Titanium, Ti | 0.1 max |
| Remainder (total) | 0.15 max |
| Aluminum, Al | Remainder |
The physical properties of aluminium / aluminum 7039 alloy are outlined in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 2.74 g/cm³ | 0.0990 lb/in³ |
| Melting point | 482-638°C | 900-1180 °F |
The mechanical properties of aluminium / aluminum 7039-T64 alloy are tabulated below.
Wire Gauge (SWG):
Certification:
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength (@diameter 12.7 mm/0.500 in) | 450 MPa | 65300 psi |
| Yield strength (@diameter 12.7 mm/0.500 in) | 380 MPa | 55100 psi |
| Elongation at break (@diameter 12.7 mm/0.500 in) | 13% | 13% |
| Elastic modulus | 69.6 GPa | 10100 ksi |
| Shear strength | 255 MPa | 37000 psi |
| Hardness, Brinell (@load 500 kg; thickness 10.0 mm/1100 lb;0.394 in) | 133 | 133 |
| Hardness, Knoop (converted from Brinell hardness value) | 167 | 167 |
| Hardness, Rockwell A (converted from Brinell hardness value) | 50 | 50 |
| Hardness, Rockwell B (converted from brinell hardness value) | 81 | 81 |
| Hardness, Vickers (converted from Brinell hardness value) | 153 | 153 |
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Material | Aluminum Alloy |
| Usage/Application | Construction |
| Brand | FHA |
| Shape | Round |
| Length | 500 m |
| Packaging Type | Roll |
| Grade | Al 6063 63400 H9 Al-Mg-Si 0.5 |
Aluminium alloy 6063 is a medium strength alloy commonly referred to as an architectural alloy. It is normally used in intricate extrusions.
It has a good surface finish, high corrosion resistance, is readily suited to welding and can be easily anodised. Most commonly available as T6 temper, in the T4 condition it has good formability.
Aluminium alloy 6063 is used in:
In balustrading the rails and posts are normally in the T6 temper and formed elbows and bends are T4. T4 temper 6063 aluminium is also finding applications in hydroformed tube for chassis.
Aluminium alloy 6063/6063A also corresponds to the following standard designations and specifications:
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Chemical composition for aluminium alloy 6063 and 6063A
| Element | 6063 % Present | 6063A % Present |
|---|---|---|
| Si | 0.2 to 0.6 | 0.3 to 0.6 |
| Fe | 0.0 to 0.35 | 0.15 to 0.35 |
| Cu | 0.0 to 0.1 | 0.1 |
| Mn | 0.0 to 0.1 | 0.15 |
| Mg | 0.45 to 0.9 | 0.6 to 0.9 |
| Zn | 0.0 to 0.1 | 0.0 to 0.15 |
| Ti | 0.0 to 0.1 | 0.1 |
| Cr | 0.1 max | 0.05 |
| Al | Balance | Balance |
The most common tempers for 6063 aluminium are: