Product Details:
| Minimum Order Quantity | 50 Kg |
| Material | Alumunium Alloy |
| Grade | 6063 |
| Is It Anodised | Anodised |
| Surface Treatment | Hot Rolled |
| Usage/Application | Construction |
| Brand | FHA |
| Diameter | 350 mm |
Aluminium alloy 6063 is a medium strength alloy commonly referred to as an architectural alloy. It is normally used in intricate extrusions.
It has a good surface finish, high corrosion resistance, is readily suited to welding and can be easily anodised. Most commonly available as T6 temper, in the T4 condition it has good formability.
Aluminium alloy 6063 is used in:
In balustrading the rails and posts are normally in the T6 temper and formed elbows and bends are T4. T4 temper 6063 aluminium is also finding applications in hydroformed tube for chassis.
Aluminium alloy 6063/6063A also corresponds to the following standard designations and specifications:
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Chemical composition for aluminium alloy 6063 and 6063A
| Element | 6063 % Present | 6063A % Present |
|---|---|---|
| Si | 0.2 to 0.6 | 0.3 to 0.6 |
| Fe | 0.0 to 0.35 | 0.15 to 0.35 |
| Cu | 0.0 to 0.1 | 0.1 |
| Mn | 0.0 to 0.1 | 0.15 |
| Mg | 0.45 to 0.9 | 0.6 to 0.9 |
| Zn | 0.0 to 0.1 | 0.0 to 0.15 |
| Ti | 0.0 to 0.1 | 0.1 |
| Cr | 0.1 max | 0.05 |
| Al | Balance | Balance |
The most common tempers for 6063 aluminium are:
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Material | Aluminum Alloy |
| Grade | 3004 |
| Usage/Application | Construction |
| Brand | FHA |
| Diameter | 350 mm |
| Shape | Round |
Aluminium / Aluminum alloys have high corrosion resistance. Their strength can be reduced when they are exposed to high temperatures. However, their strength can be increased at subzero temperatures. Aluminium / Aluminum 3004 alloy is an alloy containing manganese and magnesium.
The following datasheet gives more details about Aluminium / Aluminum 3004 alloy.
The following table shows the chemical composition of Aluminium / Aluminum 3004 alloy.
| Element | Content (%) |
|---|---|
| Aluminium / Aluminum , Al | 97.8 |
| Manganese, Mn | 1.2 |
| Magnesium, Mg | 1 |
The physical properties of Aluminium / Aluminum 3004 alloy are tabulated below.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 2.6-2.8 g/cm3 | 0.0939- 0.101 lb/in3 |
| Melting point | 633°C | 1170°F |
The mechanical properties of Aluminium / Aluminum 3004 alloy are outlined in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 215 MPa | 31183 psi |
| Yield strength | 170 MPa | 24656 psi |
| Shear strength | 115 MPa | 16680 psi |
| Fatigue strength | 105 MPa | 15229 psi |
| Elastic modulus | 70-80 GPa | 10153-11603 ksi |
| Poisson's ratio | 0.33 | 0.33 |
| Elongation | 10% | 10% |
| Hardness | 52 | 52 |
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Grade | 5056 |
| Brand | FHA |
| Material | Aluminum Alloy |
| Application | Industry and Construction |
| Shape | Round |
| Diameter | 500 mm |
Aluminum alloys contain have strong corrosion resistance characteristics and high electrical conductivity. These alloys obtain high strength when exposed to subzero temperatures and experience a decrease in strength when exposed toat high temperatures ranging between 200 and 250°C (392 and 482°F). Hence, Aaluminum alloys are known as good low-temperature alloys and are sensitive to high temperatures ranging between 200 and 250°C (392 and 482°F).
The following datasheet provides an overview of the aluminum 5056 alloy.
The chemical composition of the aluminum 5056 alloy is outlined in the following table.
| Element | Content (%) |
|---|---|
| Aluminum, Al | 95.0 |
| Magnesium, Mg | 5.0 |
| Manganese, Mn | 0.12 |
| Chromium, Cr | 0.12 |
The following table shows the physical properties of the aluminum 5056 alloy.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 2.64 g/cc | 0.0953 lb/in3 |
The mechanical properties of the aluminum 5056 alloy are displayed in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Elastic modulus | 70-80 Gpa | 10152-11603 ksi |
| Poisson's ratio | 0.33 | 0.33 |
The thermal properties of the aluminum 5056 alloy are given in the following table.
| Properties | Conditions | ||
|---|---|---|---|
| T (ºC) | Treatment | ||
| Thermal expansion | 24.1 (10-6/ºC) | 20-100 | - |
| Thermal conductivity | 112 (W/mK) | 25 | H38 |
Product Details:
| Minimum Order Quantity | 50 Kg |
| Brand | FHA |
| Surface Finish | Mill Finished |
| Grade | Al 5052 |
| Shape | Round |
| Material | Aluminium |
| Size | 3 inch |
| Application | Structure Pipe, Hydraulic Pipe, Gas Pipe |
| Unit Length | 6 m |
Aluminium alloy 5052 in H32 temper has very good corrosion resistance to seawater and marine and industrial atmosphere. It also has very good weldability and good cold formability. It is a medium to high strength alloy with a strength slightly higher than 5251 and a medium to high fatigue strength.
Properties:
Alloy 5052-H32 has a range of useful properties:
Applications:
Amongst the applications for Alloy 5052 are:
Chemical Composition:
Product Details:
| Minimum Order Quantity | 50 Piece |
| Surface Finish | Finished Polished |
| Material Grade | Al 1060 |
| Shape | Round |
| Material | Aluminium |
| Single Piece Length | 18 meter |
| Brand | FHA |
| Diameter | 500 mm |
| Finishing | Smooth |
| Usage/Application | Construction |
| Tolerance | +0.05/-0.05 |
| Certification | 3.1 |
Aluminium / Aluminum alloys are known for their strong corrosion resistance characteristics. These alloys are sensitive to high temperatures and experience an increase in strength at subzero temperatures. Aluminium / Aluminum alloys are good low-temperature alloys.
Aluminium / Aluminum 1060 alloy is a low strength and pure Aluminium / Aluminum alloy with good corrosion resistance characteristic.
The following datasheet provides an overview of Aluminium / Aluminum 1060 alloy.
The chemical composition of Aluminium / Aluminum 1060 alloy is outlined in the following table.
| Element | Content (%) |
|---|---|
| Aluminium / Aluminum, Al | 99.60 (min) |
The following table shows the physical properties of Aluminium / Aluminum 1060 alloy.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 2.7 g/cm3 | 0.0975 lb/in3 |
| Melting point | 649°C | 1200°F |
The mechanical properties of Aluminium / Aluminum 1060 alloy are displayed in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Elastic modulus | 70-80 GPa | 10152-11603 ksi |
| Poisson's ratio | 0.33 | 0.33 |
The thermal properties of Aluminium / Aluminum 1060 alloy are given in the following table.
| Properties | Conditions | ||
|---|---|---|---|
| T (ºC) | Treatment | ||
| Thermal expansion | 23.6 (10-6/ºC) | 20-100 | - |
| Thermal conductivity | 234 (W/mK) | 25 | H18 |
Product Details:
| Minimum Order Quantity | 50 Kg |
| Brand | FHA |
| Material | Aluminium Alloy |
| Grade | Al 8011 |
| Single Piece Length | 36 meter |
| Usage/Application | Construction |
| Diameter | 500 mm |
| Shape | Round |
Apart from iron, aluminium / aluminum is currently the next most widely used metal in the world. This is due to the fact that aluminium / aluminum has a unique combination of attractive properties. Properties such as its low weight, corrosion resistance, and easy maintenance of final product, have ensured that this metal and its alloys will be in use for a very long time.
Aluminium / aluminum 8011 alloy is a wrought alloy. The following datasheet will provide more details about aluminium / aluminum 8011 alloy.
The following table shows the chemical composition of aluminium / aluminum 8011 alloy.
| Element | Content (%) |
|---|---|
| Aluminum, Al | 97.3 - 98.9 |
| Iron, Fe | 0.60 - 1 |
| Silicon, Si | 0.50 - 0.90 |
| Manganese, Mn | ≤ 0.20 |
| Zinc, Zn | ≤ 0.10 |
| Copper, Cu | ≤ 0.10 |
| Titanium, Ti | ≤ 0.080 |
| Chromium, Cr | ≤ 0.050 |
| Magnesium, Mg | ≤ 0.050 |
| Remainder (each) | ≤ 0.050 |
| Remainder (total) | ≤ 0.15 |