Product Details:
Minimum Order Quantity | 50 Kilogram |
Material | Cupro-Nickel |
Material Grade | 70/30 |
Usage/Application | Construction |
Shape | Rectangular |
Thickness | 10 mm |
Surface Treatment | Hot Rolled |
UNS | C71500 |
Standard | AMS 4881 DIN 2.0882 |
Related Specifications of 70/30:
Cu rem, Ni 30%, Fe 0.7%, Mn 1.0%
Mechanical Properties of 70/30Ultimate Tensile Strength (N/mm²) | Proof Stress (N/mm²) | Elongation (%) | Hardness (HB) |
---|---|---|---|
310 | 27 | 80-120 |
Offshore marine: Salt water flanges, salt water piping and pipe fittings, valve bodies, sea water intakes, pipe fittings, water boxes, propeller sleeves, pump bodies and parts
Chemical processing: Heat exchanger and cooling plant, evaporator tubes, distiller tubes, refrigerator and condenser components
Other: Welding backing rings, flexible metal hose, weld wire and boiler parts
With decades of experience and a huge range of stock, Columbia Metals is an industry leader in the supply of 70/30 and other high quality specialist engineering alloys.
Product Details:
Minimum Order Quantity | 50 Kg |
Thickness | 200 mm |
Material Grade | Inconel X750 |
Standard | UNS N07752, UNS N07750, W Nr 2.4669 |
Type | Nickel Plate, Alloy Steel plate |
Usage/Application | Industry |
Alloy | With Alloy |
W.Nr. | W Nr 2.4669 |
Uns | UNS N07752,UNS N07750 |
Grade | Inconel, Alloy, Hastalloy |
Alloy X-750 is a nickel-chromium alloy which has been made precipitation-hardenable by the additions of aluminum and titanium. Alloy X-750 has good resistance to corrosion and oxidation along with high tensile and creep rupture properties at temperature up to 1300ºF (700ºC). Due to X-750's excellent relaxation resistance it is useful for applications as high-temperature springs and bolts, X-750 is also used in gas turbines, rocket engines, nuclear reactors, pressure vessels, tooling and aircraft structures.
AMS 5667 - 1625°F/24hr, AC + 1300°F/20 hr, AC (Equalising plus precipitation treatment). AMS 5667 Rod, Bars and Forgings have high strength and notch rupture ductility up to 1100°F
AMS 5668 - 2100°F anneal + 1550°F/24 hr, AC, +1300°F/20hr, AC (triple heat treatment). AMS 5668 has maximum creep, relaxation and rupture strength above about 1100°F.
AMS 5670 - 1800°F anneal + 1350°F/8hr, FC to 1150°F. Hold at 1150°F for total precipitation-treating time 18 hr, AC (solution treatment plus furnace cool precipitation treatment). Due to the heat treatments AMS 5670, AMS 5671 and AMS 5747 have increased tensile properties and reduced heat treatment time service up to about 1100°F.
AMS 5542 - 1300°F/20hr, AC (Constant-temperature precipitation treatment). AMS 5542 has high strength up to 1300°F
AMS 5598 - 1350°F/8hr, FC to 1150°F, hold at 1150°F for total precipitation-treating time of 18hr, AC (furnace-cool precipitation treatment. AMS 5598 has high strength up to 1300°F (Increased tensile properties to about 1100°F).
With heat treatment 1400°F/1hr, FC to 1150°F hold at 1150°F for total time of 6hr, AC.
Chemical Composition Limits | ||||||||||||
Weight % | Ni +(Co) | Cr | Fe | Ti | Al | Nb + (Ta) | Mn | Si | S | Cu | C | Co |
X-750 UNS N07750 | 70 min | 14-17 | 5-9 | 2.25-2.75 | 0.40-1.0 | 0.70-1.2 | 1 max | 0.50 max | 0.01 max | 0.50 max | 0.08 max | 1 max |
UNS N07752 is available in billets for forging. UNS N0772 has limits of 0.05% on both Carbon and Cobalt |
Specifications:
Rod | ASTM B 637, ASME SB 637, ISO 9723, ISO9724, ISO9725, AMS 5667, AMS 5668, AMS 5669, AMS 5670, AMS 5671, AMS 5747, EN10269 |
Bar | ASTM B 637, ASME SB 637, ISO 9723, ISO9724, ISO9725, AMS 5667, AMS 5668, AMS 5669, AMS 5670, AMS 5671, AMS 5747, EN10269 |
Forging Stock | ASTM B 637, ASME SB 637, ISO 9723, ISO9724, ISO9725, AMS 5667, AMS 5668, AMS 5669, AMS 5670, AMS 5671, AMS 5747, EN10269 |
Plate | ISO 6208, AMS 5542 and AMS 5598 |
Sheet | ISO 6208, AMS 5542 and AMS 5598 |
Strip | ISO 6208, AMS 5542 and AMS 5598 |
Wire | BS HR 505, AMS 5698, AMS 5699 |
Other | UNS N07750, W.Nr 2.4669, Inconel X750 (tradename), UNS N07752 |
Additional Information: