Beryllium Copper UNS C17200

Providing you the best range of beryllium copper and beryllium copper uns with effective & timely delivery.

Beryllium Copper

Beryllium Copper
  • Beryllium Copper
Get Best Quote
Approx. Price: Rs 1,500 / KgGet Latest Price

UNS C17200 beryllium copper alloys are ductile and produced in mill hardened and heat treatable tempers. These alloys are used for all applications, which require high strength, stiffness and good conductivity. The tensile strength of C17200 copper is over 1380 MPa (200 ksi).

The following datasheet will explain about UNS C17200 beryllium copper alloys.

Chemical Composition

The following table shows the chemical composition of UNS C17200 copper.

Element

Content (%)

Cu

97.9

Be

1.9

Co

0.20

Physical Properties

The physical properties of UNS C17200 copper are given in the following table.

Properties

Metric

Imperial

Density (during age hardening, 2% max. decrease in length and 6% max. increase in density)

8.25 g/cm3

0.298 lb/in3

Melting point

866°C

1590°F

Mechanical Properties

The mechanical properties of UNS C17200 copper are tabulated below.

Properties

Metric

Imperial

Hardness, Rockwell B

80.0 - 85.0

80.0 - 85.0

Tensile strength, ultimate

1280 - 1480 MPa

186000 - 215000 psi

Tensile strength, yield

965 - 1205 MPa

140000 - 174800 psi

Elongation at break

15.0 - 30.0%

15.0 - 30.0%

Modulus of elasticity

125 - 130 GPa

18100 - 18900 ksi

Poissons ratio

0.300

0.300

Machinability (UNS C36000 (free-cutting brass) = 100%)

20%

20%

Shear modulus

50.0 GPa

7250 ksi

Request
Callback


Additional Information:

  • Item Code: BerylliumCopper_UNSC17200_AlloyC17200_ForgedBlock
  • Minimum Order Quantity: 50 Kg
Yes! I am Interested

Beryllium Copper UNS

Beryllium Copper UNS
  • Beryllium Copper UNS
Get Best Quote
Approx. Price: Rs 1,500 / KgGet Latest Price
Introduction

UNS C17300 beryllium copper alloys are heat treatable, ductile and can be mill hardened. They offer tensile strength of 1380 MPa (200 ksi). These steels are suitable for applications requiring good conductivity, high strength and stiffness.

This article will give an overview of UNS C17300 beryllium copper alloys.

Chemical Composition

The following table shows the chemical composition of UNS C17300 copper.

ElementContent (%)
Cu97.7
Be1.9
Co0.40
Physical Properties

The physical properties of UNS C17300 copper are given in the following table.

PropertiesMetricImperial
Density (during age hardening, 2% max. decrease in length and 6% max. increase in density)8.25 g/cm30.298 lb/in3
Melting point866°C1590°F
Mechanical Properties

The mechanical properties of UNS C17300 copper are tabulated below.

PropertiesMetricImperial
Hardness, Rockwell B80.0 - 85.080.0 - 85.0
Tensile strength, ultimate515 - 585 MPa74700 - 84800 psi
Tensile strength, yield275 - 345 MPa39900 - 50000 psi
Elongation at break15.0 - 30.0%15.0 - 30.0%
Modulus of elasticity125 - 130 GPa18100 - 18900 ksi
Poissons ratio0.3000.300
Machinability (UNS C36000 (free-cutting brass) = 100%)20%20%
Shear modulus50.0 GPa7250 ksi
Request
Callback


Additional Information:

  • Item Code: BerylliumCopper_UNSC17300_ForgedBlock
  • Minimum Order Quantity: 50 Kg
Yes! I am Interested
X

Explore more products



Reach Us
Anil Gupta (Sales Manager)
B-12A, Flox Chambers, Tata Road No. 1 Opera House
Mumbai- 400004, Maharashtra, India



Call Us

Share Us

F GT L


Send E-mailSend SMS