FountainHead Alloys
Opera House, Mumbai, Maharashtra
SEND SMS
SEND EMAIL
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Brand | IMPORTED |
| Usage | Construction , Household Repair, Manufacturing |
| Size | 5 TO 500MM DIA |
| Single Piece Length | 36 meter, 6 meter, 3 meter, >36 meter, 18 meter |
| Blue | 5000 |
Additional Information:
Product Details:
| Blue | 4500 |
| Nominal Size | 1/2 inch, 3/4 inch, 1 inch, 2 inch, 3 inch, >3 inch |
| Length | 3m, 6m, 30m, 100m |
| Shape | Round, Square, Rectangular, Oval |
| Steel Grade | SS316, SS316L, SS304, SS304L, ASTM A240 |
Additional Information:
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Single Piece Length | >36 meter, 6 meter, 3 meter, 18 meter |
| Application | Food Products, Drinking Water, Chemical Handling, Gas Handling, Utilities Water |
| Brand | IMPORTED |
| Size/Diameter | 1 inch, 2 inch, 3 inch, 1/2 inch, >4 inch, 4 inch |
| Blue | 4000 |
The management team are amongst the most experienced professionals in the market. Supported by professional metallurgists and technicians, not only provide access to the largest range of high-tec metals in Europe, but also access to the broadest range of expertise.
The unique combination of access to stock, expertise and rapid delivery reduces lead times and can eliminate costly production delays.
The range of materials includes:
• Titanium Alloys
• Nickel Alloys
• Steels
A-286 Iron-Based Super AlloyA-286 is an age-hardenable iron base superalloy for applications requiring high strength from -320°F up to 1000°F long time, 1300-1500°F short time. Oxidation resistance is high for continuous service to 1500°F, intermittent to 1800°F. Aqueous corrosion resistance is comparable to 316/L stainless.
Applications for A-286Typical Applications for the A-286 include:
• Jet engine components
• High temperature fasteners, springs
• Non-magnetic cryogenic equipment
Composition of A-286The composition range for A-286 is provided in table 1.
Table 1. Composition of A-286.
Chemistry, % | Min | Max |
Chromium | 13.50 | 16.00 |
Nickel | 24.00 | 27.00 |
Molybdenum | 1.00 | 1.50 |
Cobalt | - | 1.00 |
Vanadium | 0.10 | 0.50 |
Aluminum | - | 0.35 |
Titanium | 1.90 | 2.35 |
Boron | 0.003 | 0.010 |
Carbon | - | 0.08 |
Iron | remainder | |
Manganese | - | 2.00 |
Silicon | - | 1.00 |
Phosphorus | - | 0.025 |
Sulfur | - | 0.025 |
Additional Information:
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Blue | 4500 |
| Brand | IMPORTED |
| Size | 5 TO 500MM |
| Quantity Per Pack | 100Kg |
The management team are amongst the most experienced professionals in the market. Supported by professional metallurgists and technicians, not only provide access to the largest range of high-tec metals in Europe, but also access to the broadest range of expertise.
The unique combination of access to stock, expertise and rapid delivery reduces lead times and can eliminate costly production delays.
Range of materials includes:
• Titanium Alloys
• Nickel Alloys
• Steels
A-286 Iron-Based Super AlloyA-286 is an age-hardenable iron base superalloy for applications requiring high strength from -320°F up to 1000°F long time, 1300-1500°F short time. Oxidation resistance is high for continuous service to 1500°F, intermittent to 1800°F. Aqueous corrosion resistance is comparable to 316/L stainless.
Applications for A-286Typical Applications for the A-286 include:
• Jet engine components
• High temperature fasteners, springs
• Non-magnetic cryogenic equipment
Composition of A-286The composition range for A-286 is provided in table 1.
Table 1. Composition of A-286.
Chemistry, % | Min | Max |
Chromium | 13.50 | 16.00 |
Nickel | 24.00 | 27.00 |
Molybdenum | 1.00 | 1.50 |
Cobalt | - | 1.00 |
Vanadium | 0.10 | 0.50 |
Aluminum | - | 0.35 |
Titanium | 1.90 | 2.35 |
Boron | 0.003 | 0.010 |
Carbon | - | 0.08 |
Iron | remainder | |
Manganese | - | 2.00 |
Silicon | - | 1.00 |
Phosphorus | - | 0.025 |
Sulfur | - | 0.025 |
Additional Information:
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Design | Standard |
| Size | 5 TO 500MM |
| Brand | IMPORTED |
| Blue | 4500 |
The management team are amongst the most experienced professionals in the market. Supported by professional metallurgists and technicians, not only provide access to the largest range of high-tec metals in Europe, but also access to the broadest range of expertise.
The unique combination of access to stock, expertise and rapid delivery reduces lead times and can eliminate costly production delays.
The range of materials includes:
• Titanium Alloys
• Nickel Alloys
• Steels
A-286 Iron-Based Super AlloyA-286 is an age-hardenable iron base superalloy for applications requiring high strength from -320°F up to 1000°F long time, 1300-1500°F short time. Oxidation resistance is high for continuous service to 1500°F, intermittent to 1800°F. Aqueous corrosion resistance is comparable to 316/L stainless.
Applications for A-286Typical Applications for the A-286 include:
• Jet engine components
• High temperature fasteners, springs
• Non-magnetic cryogenic equipment
Composition of A-286The composition range for A-286 is provided in table 1.
Table 1. Composition of A-286.
Chemistry, % | Min | Max |
Chromium | 13.50 | 16.00 |
Nickel | 24.00 | 27.00 |
Molybdenum | 1.00 | 1.50 |
Cobalt | - | 1.00 |
Vanadium | 0.10 | 0.50 |
Aluminum | - | 0.35 |
Titanium | 1.90 | 2.35 |
Boron | 0.003 | 0.010 |
Carbon | - | 0.08 |
Iron | remainder | |
Manganese | - | 2.00 |
Silicon | - | 1.00 |
Phosphorus | - | 0.025 |
Sulfur | - | 0.025 |
Additional Information:
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Length | 5 TO 500MM DIA |
| Steel Grade | Incoloy A-286 |
| Blue | 4000 |
Additional Information:
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Thickness | 0.2mm-5mm |
| Grade | 1000 Series |
| Type | Plate |
Aluminium alloy 6061 is one of the most extensively used of the 6000 series aluminium alloys. It is a versatile heat treatable extruded alloy with medium to high strength capabilities. Composition Table 1. Typical composition of aluminium alloy 6061
| |||||||||||||||||||||||||
Key Properties | |||||||||||||||||||||||||
Typical properties of aluminium alloy 6061 include: • Medium to high strength • Good toughness • Good surface finish • Excellent corrosion resistance to atmospheric conditions • Good corrosion resistance to sea water • Can be anodized • Good weldability and brazability • Good workability • Widely available Physical Properties Density: 2.7 g/cm3 Melting Point: Approx 580°C Modulus of Elasticity: 70-80 GPa Poissons Ratio: 0.33 Mechanical Properties
Thermal Properties Co-Efficient of Thermal Expansion (20-100°C): 23.5x10-6 m/m.°C Thermal Conductivity: 173 W/m.K
|
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Thickness | 0.2mm-5mm |
| Grade | 1000 Series |
| Surface Treatment | Coated |
Aluminium 5754 has excellent corrosion resistance especially to seawater and industrially polluted atmospheres.
It has higher strength than 5251. This high strength makes Aluminium 5754 highly suited to flooring applications.
After rolling, Aluminium 5754 spontaneously softens until it reaches a stable condition.
Chemical Composition of Aluminium 5754Table 1. Chemical composition for aluminium alloy 5754
| Element | % Present |
|---|---|
| Si | 0.4 |
| Fe | 0.4 |
| Mn | 0.5 |
| Mg | 2.6-3.2 |
| Al | Balance |
Table 2 (a). Mechanical properties for aluminium alloy 5754 H111 Treadplate
| BS EN 485-2:2008 Sheet 0.2mm to 6.00mm | |
|---|---|
| Property | Value |
| Proof Stress | 60 Min MPa |
| Tensile Strength | 160 - 200 MPa |
| Elongation A50 mm | 12 Min % |
| Hardness Brinell | 44 HB |
*Properties above are for material in the H111 condition.
Some thicknesses have a slightly higher minimum elongation requirement.
Table 2 (b). Mechanical properties for aluminium alloy 5754 H114
| BS EN 485-2:2008 Aluminium Sheet 0.2mm to 6.00mm | |
|---|---|
| Property | Value |
| Proof Stress | 80 Min MPa |
| Tensile Strength | 190 - 260 MPa |
| Elongation A50 mm | 12 Min % |
| Hardness Brinell | 52 HB |
*Properties above are for material in the H114 condition
Table 2 (c). Mechanical properties for aluminium alloy 5754 H22
| BS EN 485-2:2008 Sheet Plate 0.2mm to 40mm | |
|---|---|
| Property | Value |
| Proof Stress | 130 Min MPa |
| Tensile Strength | 220 - 270 MPa |
| Elongation A50 mm | 7 Min % |
| Hardness Brinell | 63 HB |
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Surface Treatment | Coated |
| Thickness | 0-1 mm ,1-2 mm, 2-3 mm, 3-4 mm |
| Width | 15000mm,up to15000mm |
Aluminium alloy 6061 is one of the most extensively used of the 6000 series aluminium alloys. It is a versatile heat treatable extruded alloy with medium to high strength capabilities. Composition Table 1. Typical composition of aluminium alloy 6061
| |||||||||||||||||||||||||
Key Properties | |||||||||||||||||||||||||
Typical properties of aluminium alloy 6061 include: • Medium to high strength • Good toughness • Good surface finish • Excellent corrosion resistance to atmospheric conditions • Good corrosion resistance to sea water • Can be anodized • Good weldability and brazability • Good workability • Widely available Physical Properties Density: 2.7 g/cm3 Melting Point: Approx 580°C Modulus of Elasticity: 70-80 GPa Poissons Ratio: 0.33 Mechanical Properties
Thermal Properties Co-Efficient of Thermal Expansion (20-100°C): 23.5x10-6 m/m.°C |
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Thickness | 0.2mm-200mm |
| Application | Decoration, Construction |
| Grade | 6000 Series |
Aluminum alloys contain strong corrosion resistance. These alloys are good low-temperature alloys. Aluminium / Aluminum alloys are sensitive to high temperatures ranging between 200 and 250°C (392 and 482°F). The strength of these alloys increases when exposed to subzero temperatures and the strength decreases when exposed to high temperatures.
The following datasheet provides an overview of Aluminium / Aluminum 5454 alloy.
Chemical CompositionThe chemical composition of Aluminium / Aluminum 5454 alloy is outlined in the following table.
| Element | Content (%) |
|---|---|
| Aluminium / Aluminum, Al | 96.3 |
| Magnesium, Mg | 2.7 |
| Chromium, Cr | 0.12 |
| Manganese, Mn | 0.8 |
The following table shows the physical properties of Aluminium / Aluminum 5454 alloy.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 2.6-2.8 g/cm3 | 0.0939-0.1011 lb/in3 |
| Melting point | 607°C | 1125°F |
The mechanical properties of Aluminium / Aluminum 5454 alloy are displayed in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Elastic modulus | 70-80 GPa | 10152-11603 ksi |
| Poisson's ratio | 0.33 | 0.33 |
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Material | Aluminum |
| Application | Industry and construction |
| Shape | Square |
Aluminum alloys contain have strong corrosion resistance characteristics and high electrical conductivity. These alloys obtain high strength when exposed to subzero temperatures and experience a decrease in strength when exposed toat high temperatures ranging between 200 and 250°C (392 and 482°F). Hence, Aaluminum alloys are known as good low-temperature alloys and are sensitive to high temperatures ranging between 200 and 250°C (392 and 482°F).
The following datasheet provides an overview of the aluminum 5056 alloy.
Chemical CompositionThe chemical composition of the aluminum 5056 alloy is outlined in the following table.
| Element | Content (%) |
|---|---|
| Aluminum, Al | 95.0 |
| Magnesium, Mg | 5.0 |
| Manganese, Mn | 0.12 |
| Chromium, Cr | 0.12 |
The following table shows the physical properties of the aluminum 5056 alloy.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 2.64 g/cc | 0.0953 lb/in3 |
The mechanical properties of the aluminum 5056 alloy are displayed in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Elastic modulus | 70-80 Gpa | 10152-11603 ksi |
| Poisson's ratio | 0.33 | 0.33 |
The thermal properties of the aluminum 5056 alloy are given in the following table.
| Properties | Conditions | ||
|---|---|---|---|
| T (ºC) | Treatment | ||
| Thermal expansion | 24.1 (10-6/ºC) | 20-100 | - |
| Thermal conductivity | 112 (W/mK) | 25 | H38 |
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Surface Treatment | Mill Finished |
| Grade | 6000 Series |
| Application | Industry and construction |
Aluminium / Aluminum alloys have strong corrosion resistance characteristics and high electrical conductivity. These alloys are sensitive to high temperatures ranging between 200 and 250°C (392 and 482°F) and tend to lose their strength. They are good low-temperature alloys and gain strength when exposed to subzero temperatures.
Aluminium / Aluminum 5086 alloy is a high strength structural alloy. The following datasheet provides an overview of Aluminium / Aluminum 5086 alloy.
Chemical CompositionThe chemical composition of Aluminium / Aluminum 5086 alloy is outlined in the following table.
| Element | Content (%) |
|---|---|
| Al | 95.4 |
| Mg | 4.0 |
| Cr | 0.15 |
| Mn | 0.4 |
The following table shows the physical properties of Aluminium / Aluminum 5086 alloy.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 2.65 g/cm3 | 0.0957 lb/in3 |
| Melting point | 588°C | 1090°F |
The mechanical properties of Aluminium / Aluminum 5086 alloy are displayed in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Elastic modulus | 70-80 GPa | 10152-11603 ksi |
| Poisson's ratio | 0.33 | 0.33 |
The thermal properties of Aluminium / Aluminum 5086 alloy are given in the following table.
| Properties | Conditions | ||
|---|---|---|---|
| T (ºC) | Treatment | ||
| Thermal expansion | 23.9 (10-6/ºC) | 20-100 | - |
| Thermal conductivity | 127 (W/mK) | 25 | All |
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Material | Aluminum |
| Application | Industry and construction |
| Thickness | 0.2mm-5mm |
Aluminium alloy 5005 contains nominally 0.8% magnesium. It has medium strength, good weldability, and good corrosion resistance in marine atmospheres. It also has the low density and excellent thermal conductivity common to all aluminium alloys. It is the most commonly used grade of aluminium in sheet and plate form.
Aluminium alloy 5005 is a lean aluminium magnesium alloy which can be hardened by cold work: it is not heat treatable to higher strength.
Austral Wright Metals can supply this alloy as plate, sheet and strip. See Austral Wright Metals Catalogue for normal stock sizes and tempers.
Corrosion Resistance of Aluminium Alloy 5005Corrosion Resistance 5005 has the same high resistance to general corrosion as other non heat treatable aluminium alloys. It also has the higher resistance to slightly alkaline conditions common to the 5000 series alloys. The atmospheric corrosion resistance of 5005 is similar to that of 3003.
When anodised to improve corrosion resistance, the film on 5005 is clearer than on 3003, and gives better colour match with 6063 architectural extrusions.
The corrosion resistance of aluminium alloys relies on a protective surface oxide film, which when damaged is readily repaired by the rapid reaction between aluminium and oxygen. However, the high reactivity of the base metal can give rapid corrosion if the film cannot be repaired, so aluminium alloys are not suitable for use with reducing media.
Since aluminium is a reactive metal, it may corrode more quickly when in electrical contact with most other metals. The prediction of galvanic corrosion is complex, please consult Austral Wright Metals for specific advice.
Applications of Aluminium Alloy 5005Typical Applications of aluminium alloy 5005 include:
• Architectural applications
• General sheet metal work
• High strength foil.
Chemical Composition of Aluminium Alloy 5005Table 1. Chemical composition of Aluminium 5005.
Element | % | Element | % |
Aluminium | Balance | Manganese | 0.20 max |
Magnesium | 0.50 – 1.10 | Chromium | 0.10 max |
Silicon | 0.30max | Zinc | 0.25 max |
Iron | 0.07 max | Others, each | 0.05 max |
Copper | 0.20 max | Others, total | 0.15 max |
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Grade | 6000 Series |
| Material | Aluminium |
| Surface Treatment | Coated, Painted, Hot Rolled |
Aluminium / aluminum 3000 series alloys provide a wide range of mechanical properties coupled with excellent corrosion resistance, weldability and formability.
Aluminium/aluminum 3005 alloy is a non-heat treatable wrought alloy with manganese as the key alloying element.
The following datasheet will provide more details about aluminium / aluminum 3005 alloy.
Chemical CompositionThe following table shows the chemical composition of aluminium / aluminum 3005-T14 alloy.
| Element | Content (%) |
|---|---|
| Aluminum, Al | 95.7 - 98.8 |
| Manganese, Mn | 1- 1.5 |
| Iron, Fe | ≤ 0.70 |
| Silicon, Si | ≤ 0.60 |
| Copper, Cu | ≤ 0.30 |
| Zinc, Zn | ≤ 0.25 |
| Magnesium, Mg | 0.20 - 0.60 |
| Chromium, Cr | ≤ 0.10 |
| Titanium, Ti | ≤ 0.10 |
| Other (each) | ≤ 0.050 |
| Other (total) | ≤ 0.15 |
The physical properties of aluminium / aluminum 3005-T14 alloy are outlined in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 2.73 g/cm³ | 0.0986 lb/in³ |
| Melting point | 630 - 655°C | 1170 - 1210 °F |
The mechanical properties of aluminium / aluminum 3005-T14 alloy are tabulated below.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 180 MPa | 26100 psi |
| Yield strength | 165 MPa | 23900 psi |
| Elongation | 7% | 7% |
| Elastic modulus | 69 GPa | 10000 ksi |
| Shear strength | 110 MPa | 16000 psi |
| Hardness, Brinell (@load 500 kg; thickness 10.0 mm) | 49 | 49 |
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Material | Aluminium |
| Thickness | 0.2mm-5mm |
| Width | 100mm--1000mm |
Aluminium alloy 1050 is a popular grade of aluminium for general sheet metal work where moderate strength is required.
Aluminium alloy 1050 is known for its excellent corrosion resistance, high ductility and highly reflective finish.
Chemical Composition of Aluminium Alloy 1050Table 1. Chemical composition for aluminium alloy 1050
| Element | % Present |
|---|---|
| Cu | 0-0.05 |
| Mg | 0-0.05% |
| Si | 0-0.25% |
| Fe | 0-0.4% |
| Mn | 0-0.05% |
| Zn | 0-0.07% |
| Ti | 0-0.05% |
| Al | Balance |
Table 2. Mechanical properties for aluminium alloy 1050 H14
| BS EN 485-2:2008 Sheet 0.2mm to 6.00mm | |
|---|---|
| Property | Value |
| Proof Stress | 85 Min MPa |
| Tensile Strength | 105 - 145 MPa |
| Hardness Brinell | 34 HB |
| Elongation A | 12 Min % |
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Type | Plate |
| Surface Treatment | Coated |
| Thickness | 0.2mm-5mm |
UNS C17200 beryllium copper alloys are ductile and produced in mill hardened and heat treatable tempers. These alloys are used for all applications, which require high strength, stiffness and good conductivity. The tensile strength of C17200 copper is over 1380 MPa (200 ksi).
The following datasheet will explain about UNS C17200 beryllium copper alloys.
Chemical Composition
The following table shows the chemical composition of UNS C17200 copper.
Element | Content (%) |
Cu | 97.9 |
Be | 1.9 |
Co | 0.20 |
Physical Properties
The physical properties of UNS C17200 copper are given in the following table.
Properties | Metric | Imperial |
Density (during age hardening, 2% max. decrease in length and 6% max. increase in density) | 8.25 g/cm3 | 0.298 lb/in3 |
Melting point | 866°C | 1590°F |
Mechanical Properties
The mechanical properties of UNS C17200 copper are tabulated below.
Properties | Metric | Imperial |
Hardness, Rockwell B | 80.0 - 85.0 | 80.0 - 85.0 |
Tensile strength, ultimate | 1280 - 1480 MPa | 186000 - 215000 psi |
Tensile strength, yield | 965 - 1205 MPa | 140000 - 174800 psi |
Elongation at break | 15.0 - 30.0% | 15.0 - 30.0% |
Modulus of elasticity | 125 - 130 GPa | 18100 - 18900 ksi |
Poissons ratio | 0.300 | 0.300 |
Machinability (UNS C36000 (free-cutting brass) = 100%) | 20% | 20% |
Shear modulus | 50.0 GPa | 7250 ksi |
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Thickness | 0.04-5mm |
| Width | 10~200mm |
| Grade | Copper Alloy |
UNS C17200 beryllium copper alloys are ductile and produced in mill hardened and heat treatable tempers. These alloys are used for all applications, which require high strength, stiffness and good conductivity. The tensile strength of C17200 copper is over 1380 MPa (200 ksi).
The following datasheet will explain about UNS C17200 beryllium copper alloys.
Chemical Composition
The following table shows the chemical composition of UNS C17200 copper.
Element | Content (%) |
Cu | 97.9 |
Be | 1.9 |
Co | 0.20 |
Physical Properties
The physical properties of UNS C17200 copper are given in the following table.
Properties | Metric | Imperial |
Density (during age hardening, 2% max. decrease in length and 6% max. increase in density) | 8.25 g/cm3 | 0.298 lb/in3 |
Melting point | 866°C | 1590°F |
Mechanical Properties
The mechanical properties of UNS C17200 copper are tabulated below.
Properties | Metric | Imperial |
Hardness, Rockwell B | 80.0 - 85.0 | 80.0 - 85.0 |
Tensile strength, ultimate | 1280 - 1480 MPa | 186000 - 215000 psi |
Tensile strength, yield | 965 - 1205 MPa | 140000 - 174800 psi |
Elongation at break | 15.0 - 30.0% | 15.0 - 30.0% |
Modulus of elasticity | 125 - 130 GPa | 18100 - 18900 ksi |
Poissons ratio | 0.300 | 0.300 |
Machinability (UNS C36000 (free-cutting brass) = 100%) | 20% | 20% |
Shear modulus | 50.0 GPa | 7250 ksi |
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Application | Industry and construction |
| Grade | 6000 Series |
| Thickness | 0.2mm-350mm |
Aluminium / aluminum is found as a part of over 270 different minerals, making it the third most abundantly available element in the Earth’s crust.
Aluminium / aluminum alloys are used in several components and the list is increasing every year. Aluminium / aluminum 4043 alloy is a wrought alloy type with good corrosion resistance.
The following datasheet will provide more details about aluminium / aluminum 4043 alloy.
Chemical CompositionThe following table shows the chemical composition of aluminium / aluminum 4043 alloy.
| Element | Content (%) |
|---|---|
| Aluminum, Al | 94.8 |
| Silicon, Si | 5.20 |
The physical properties of aluminium / aluminum 4043 alloy are outlined in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 2.69 g/cm3 | 0.0972 lb/in3 |
The mechanical properties of aluminium / aluminum 4043 alloy are tabulated below.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 145 MPa | 21000 psi |
| Yield strength (@diameter 12.7 mm/0.500 in) | 70 MPa | 10200 psi |
| Poisson’s ratio | 0.34 | 0.34 |
| Elongation at break (@diameter 12.7 mm/0.500 in) | 22% | 22% |
| Shear strength | 90 MPa | 13100 psi |
| Hardness, Brinell (@load 500 kg; thickness 10.0 mm/1100 lb) | 39 | 39 |
The thermal properties of aluminium / aluminum 4043 alloy are tabulated below.
| Properties | Metric | Imperial |
|---|---|---|
| Thermal expansion co-efficient (average over 20-100°C/68-212°F) | 22.1 µm/m°C | 12.3 µin/in°F |
| Thermal conductivity | 163 W/mK | 1130 BTU in/hr.ft².°F |
Equivalent materials to the aluminium / aluminum 4043 alloy are listed below:
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Surface Treatment | Coated, Painted, Hot Rolled |
| Thickness | 0.2mm-5mm |
| Grade | 1000 Series |
Aluminium / Aluminum alloys have high ductility and corrosion resistance. At subzero temperatures, their strength can be increased. However, their strength can be reduced at high temperatures of about 200-250°C. Aluminium / Aluminum 2618 alloy is an age hardenable alloy containing magnesium and copper.
The datasheet given below gives details about Aluminium / Aluminum 2618 alloy.
Chemical CompositionThe following table shows the chemical composition of Aluminium / Aluminum 2618 alloy.
| Element | Content (%) |
|---|---|
| Aluminium / Aluminum, Al | 93.7 |
| Copper, Cu | 2.30 |
| Magnesium, Mg | 1.60 |
| Iron, Fe | 1.1 |
| Nickel, Ni | 1.0 |
| Silicon, Si | 0.18 |
| Titanium, Ti | 0.07 |
The physical properties of the Aluminium / Aluminum 2618 alloy are tabulated below.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 2.6-2.8 g/cm3 | 0.0939- 0.101 lb/in3 |
| Melting point | 510°C | 950°F |
The mechanical properties of the Aluminium / Aluminum 2618 alloy are outlined in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 440 MPa | 63817 psi |
| Yield strength | 370 MPa | 53664 psi |
| Shear strength | 260 MPa | 37709 psi |
| Fatigue strength | 125 MPa | 18130 psi |
| Elastic modulus | 70-80 GPa | 10153-11603 ksi |
| Poisson's ratio | 0.33 | 0.33 |
| Elongation | 10% | 10% |
The thermal properties of the Aluminium / Aluminum 2618 alloy are given in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Thermal conductivity (@25°C/77°F) with T61 treatment | 146 W/mK | 1013 BTU in/hr.ft².°F |
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Grade | 6000 Series |
| Application | Industry and construction |
| Shape | Square |
Aluminium / aluminum is the second most widely used metal in the world today. It is a versatile metal that can be cast into any form. This lightweight metal can be welded, riveted, brazed, or resin bonded according to the requirement.
Aluminium / aluminum 1070 alloy is a wrought alloy type with good corrosion resistance. It is an excellent brazing alloy.
The following datasheet will provide more details about aluminium/ aluminum 1070 alloy.
Chemical CompositionThe following table shows the chemical composition of aluminium/aluminum 1070 alloy.
| Element | Content (%) |
|---|---|
| Aluminum, Al | ≥ 99.7 |
| Iron, Fe | ≤ 0.25 |
| Silicon, Si | ≤ 0.20 |
| Zinc, Zn | ≤ 0.040 |
| Vanadium, V | ≤ 0.050 |
| Copper, Cu | ≤ 0.040 |
| Titanium, Ti | ≤ 0.030 |
| Magnesium, Mg | ≤ 0.030 |
| Manganese, Mn | ≤ 0.030 |
| Other (each) | ≤ 0.030 |
The physical properties of aluminium/aluminum 1070 alloy are outlined in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 2.70 g/cm3 | 0.0975 lb/in3 |
The mechanical properties of aluminium / aluminum 1070-O alloy are tabulated below.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 95 MPa | 13778 psi |
Aluminium / aluminum 1070 alloy is chiefly used in the following areas: