Product Details:
Minimum Order Quantity | 50 Kg |
Material | Aluminum Alloy |
Grade | Al7020 |
Size | 500 mm |
Is It Anodised | Anodised |
Usage/Application | Construction |
Brand | FHA |
Shape | Rectangular |
The principal alloying ingredients in aluminium / aluminum alloys include manganese, magnesium, copper, zinc and silicon. The market for aluminium / aluminum and its alloys is huge. About 22 million t is newly manufactured aluminium and 7 million t is recycled aluminium scrap.
Aluminium / aluminum 7020 alloy is a heat treatable wrought alloy. Zinc forms a major part of this alloy.
The following datasheet will provide more details about aluminium / aluminum 7020 alloy.
The following table shows the chemical composition of aluminium / aluminum 7020 alloy.
Element | Content (%) |
---|---|
Zinc, Zn | 4-5 |
Magnesium, Mg | 1-1.40 |
Zirconium, Zr + Titanium, Ti | 0.80 - 0.25 |
Iron, Fe | 0.4 |
Silicon, Si | 0.35 |
Copper, Cu | 0.2 |
Chromium, Cr | 0.10 - 0.35 |
Zirconium, Zr | 0.080 - 0.20 |
Manganese, Mn | 0.050 - 0.50 |
Other (each) | 0.05 max |
Other (total) | 0.15 max |
Aluminum, Al | Remainder |
The physical properties of aluminium / aluminum 7020 alloy are outlined in the following table.
Properties | Metric | Imperial |
---|---|---|
Density | 2.78 g/cm³ | 0.100 lb/in³ |
The mechanical properties of aluminium / aluminum 7020-T6 alloy are tabulated below.
Properties | Metric | Imperial |
---|---|---|
Tensile strength (@thickness ≤100 mm/≤3.94 in) | ≥ 350 MPa | ≥ 50800 psi |
Yield strength (@thickness ≤100 mm/≤3.94 in) | ≥ 280 MPa | ≥ 40600 psi |
Elongation at break (@thickness ≤100 mm/≤3.94 in) | ≥ 10% | ≥ 10% |