Fountainhead Alloys
Opera House, Mumbai, Maharashtra
GST No. 27AKOPC9787G1ZI
TrustSEAL Verified
Call 08047643051 89% Response Rate
SEND EMAIL
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Grade | Al 6066 64423 H11 C62S |
| Material | Aluminum Alloy |
| Is It Anodised | Anodised |
| Usage/Application | Construction |
| Brand | FHA |
| Length | 12 meter |
| Diameter | 4 inch |
Aluminium / Aluminum alloys have good corrosion resistance. They tend to lose some of their strength when subjected to high temperatures. However, their strength can be increased when exposed to subzero temperatures.
The following datasheet gives an overview of Aluminium / Aluminum 6066 alloy.
The following table shows the chemical composition of Aluminium / Aluminum 6066 alloy.
| Element | Content (%) |
|---|---|
| Aluminium / Aluminum, Al | 95.7 |
| Silicon, Si | 1.40 |
| Magnesium, Mg | 1.10 |
| Copper, Cu | 1 |
| Manganese, Mn | 0.8 |
| Properties | Metric | Imperial |
|---|---|---|
| Density | 2.6-2.8 g/cm3 | 0.0939- 0.101 lb/in3 |
The mechanical properties of Aluminium / Aluminum 6066 alloy are outlined in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 150 MPa | 21755 psi |
| Yield strength | 83 MPa | 12038 psi |
| Shear strength | 97 MPa | 14069 psi |
| Fatigue strength | 110 MPa | 15954 psi |
| Elastic modulus | 70-80 GPa | 10153-11603 ksi |
| Poisson's ratio | 0.33 | 0.33 |
| Hardness | 43 | 43 |
Product Details:
| Minimum Order Quantity | 50 Kg |
| Grade | Al 6066 64423 H11 C62S |
| Shape | Rectangular |
| Color | Silver |
| Weight | 5000 kg |
| Place Of Origin | India |
| Usage/Application | Construction |
| Material | Aluminum Alloys |
| Country of Origin | Made in India |
Aluminium / Aluminum alloys have good corrosion resistance. They tend to lose some of their strength when subjected to high temperatures. However, their strength can be increased when exposed to subzero temperatures.
The following datasheet gives an overview of Aluminium / Aluminum 6066 alloy.
The following table shows the chemical composition of Aluminium / Aluminum 6066 alloy.
| Element | Content (%) |
|---|---|
| Aluminium / Aluminum, Al | 95.7 |
| Silicon, Si | 1.40 |
| Magnesium, Mg | 1.10 |
| Copper, Cu | 1 |
| Manganese, Mn | 0.8 |
| Properties | Metric | Imperial |
|---|---|---|
| Density | 2.6-2.8 g/cm3 | 0.0939- 0.101 lb/in3 |
The mechanical properties of Aluminium / Aluminum 6066 alloy are outlined in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 150 MPa | 21755 psi |
| Yield strength | 83 MPa | 12038 psi |
| Shear strength | 97 MPa | 14069 psi |
| Fatigue strength | 110 MPa | 15954 psi |
| Elastic modulus | 70-80 GPa | 10153-11603 ksi |
| Poisson's ratio | 0.33 | 0.33 |
| Hardness | 43 | 43 |
Additional Information:
Product Details:
| Minimum Order Quantity | 50 Kg |
| Material Grade | Alloys 8011 |
| Shape | Block |
| Color | Silver |
| Connection | Male, Female |
| Application | Hydraulic Pipe, Chemical Fertilizer Pipe, Gas Pipe, Structure Pipe |
| Finishing Type | Sliver Light Finish |
| Place Of Origin | FHA |
| Surface Finish | Smooth |
| Material | Aluminum |
| Country of Origin | Made in India |
| Thickness | 240 mm |
Apart from iron, aluminium / aluminum is currently the next most widely used metal in the world. This is due to the fact that aluminium / aluminum has a unique combination of attractive properties. Properties such as its low weight, corrosion resistance, and easy maintenance of final product, have ensured that this metal and its alloys will be in use for a very long time.
Aluminium / aluminum 8011 alloy is a wrought alloy. The following datasheet will provide more details about aluminium / aluminum 8011 alloy.
The following table shows the chemical composition of aluminium / aluminum 8011 alloy.
| Element | Content (%) |
|---|---|
| Aluminum, Al | 97.3 - 98.9 |
| Iron, Fe | 0.60 - 1 |
| Silicon, Si | 0.50 - 0.90 |
| Manganese, Mn | ≤ 0.20 |
| Zinc, Zn | ≤ 0.10 |
| Copper, Cu | ≤ 0.10 |
| Titanium, Ti | ≤ 0.080 |
| Chromium, Cr | ≤ 0.050 |
| Magnesium, Mg | ≤ 0.050 |
| Remainder (each) | ≤ 0.050 |
| Remainder (total) | ≤ 0.15 |
Product Details:
| Minimum Order Quantity | 50 Kilogram |
| Grade | Al 6201 64401 |
| Shape | Rectangular |
| Color | Silver |
| Usage/Application | Construction |
| Material | Aluminum Alloys |
| Size | 500 mm |
| Brand | FHA |
Aluminum alloys are known for their strong corrosion resistance. They are sensitive to high temperatures ranging between 200 and 250°C (392 and 482°F). However, the strength of Aluminium / Aluminum alloys can be enhanced at subzero temperatures, thus making them perfect low-temperature alloys.
Aluminium / Aluminum 6201 alloy is a wrought alloy type. The following datasheet will provide more details about Aluminium / Aluminum 6201 alloy.
The following table shows the chemical composition of Aluminium / Aluminum 6201 alloy.
| Element | Content (%) |
|---|---|
| Aluminum, Al | 98.5 |
| Magnesium, Mg | 0.80 |
| Silicon, Si | 0.70 |
The physical properties of Aluminium / Aluminum 6201 alloy are outlined in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 2.6-2.8 g/cm3 | 0.0939-0.1011 lb/in³ |
The mechanical properties of Aluminium / Aluminum 6201 alloy are tabulated below.
| Properties | Metric | Imperial |
|---|---|---|
| Elastic modulus | 70-80 GPa | 10152-11603 ksi |
| Poisson’s ratio | 0.33 | 0.33 |